PA66 Leona™ 14G33 ASAHI JAPAN
288
Unit Price:$3606 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 70MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Moderate heat resistance Creep resistance Fatigue resistance high strength High rigidity
- Application Areas:Engine hood parts component Automotive sector Electronic field Electrical field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | 内部方法 | 0.80 | % |
| MD | 内部方法 | 0.40 | % | |
| Wear rate | 湿 | ASTM D-1044 | 15 | ×10-6kg/1000times |
| Shrinkage rate | 干 | 旭化成方法 | 0.4/0.8 | % |
| Moisture absorption rate | 湿 | 1.7 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural strength | 干(湿) | ASTM D-790 | 325(210) | Mpa |
| Fracture elongation rate | 干(湿) | ASTM D-638 | 3(5) | % |
| tensile strength | 干(湿) | ASTM D-638 | 210(135) | Mpa |
| Cantilever beam notch impact strength | 干(湿) | ASTM D-256 | 130(170) | J/m |
| Rockwell hardness | 干(湿) | ASTM D-785 | 96(75) | M Scale |
| Scratch resistance coefficient | 干(湿) | ASTM D-790 | 10.4(6.3) | GPa |
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(-) | R scale |
| elongation | Break,23°C | ISO527-2 | 4.0 | % |
| Bending modulus | ASTMD790 | 10400 | Mpa | |
| 23°C | ISO178 | 9600 | Mpa | |
| bending strength | ASTMD790 | 325 | Mpa | |
| 23°C | ISO178 | 302 | Mpa | |
| Impact strength of simply supported beam without notch | ISO179 | 90 | kJ/m² | |
| Rockwell hardness | M-Sale | ASTMD785 | 96 | |
| Tensile modulus | 23°C | ISO527-2 | 9800 | Mpa |
| tensile strength | ASTMD638 | 210 | Mpa | |
| Break,23°C | ISO527-2 | 208 | Mpa | |
| elongation | Break | ASTMD638 | 3.0 | % |
| Rockwell hardness | R-Sale | ASTMD785 | 120 | |
| M-Sale | ISO2039-2 | 96 | ||
| R-Sale | ISO2039-2 | 120 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 260 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 260 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 250 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 250 | °C | |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 2E-05 | cm/cm/°C |
| thermal conductivity | 0.30 | W/m/K | ||
| Hot deformation temperature | 1.82MPa,干 | ASTM D-648 | 250 | °C |
| Thermal conductivity | 干 | 0.3 | W/(m.K) | |
| Hot deformation temperature | 0.46MPa,干 | ASTM D-648 | 260 | °C |
| Linear coefficient of thermal expansion | 干 | ASTM D-696 | 2 | ×10-5/K |
| Flame retardant grade | 干 | UL 94 | HB |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | 1E+15 | ohms | |
| IEC60093 | 1E+15 | ohms | ||
| Volume resistivity | ASTMD257 | 1E+15 | ohms·cm | |
| 23°C | IEC60093 | 1E+15 | ohms·cm | |
| Dielectric strength | ASTMD149 | 33 | KV/mm | |
| IEC60243-1 | 33 | KV/mm | ||
| Leakage Trace Index | 3.00mm | IEC60112 | 425 | V |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.75mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.