PA66 Leona™ FG172 ASAHI JAPAN
254
Unit Price:$4227 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Thermal stability
- Application Areas:Electrical components switch Laptop case Electronic field Electrical field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture absorption rate | 湿 | 0.9 | % | |
| Shrinkage rate | 干 | 旭化成方法 | 0.4-0.9 | % |
| Wear rate | 湿 | ASTM D-1044 | 24 | ×10-6kg/1000times |
| Shrinkage rate | TD | 内部方法 | 0.90 | % |
| MD | 内部方法 | 0.40 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2 | 9100 | Mpa |
| tensile strength | ASTMD638 | 153 | Mpa | |
| Break,23°C | ISO527-2 | 136 | Mpa | |
| elongation | Break | ASTMD638 | 2.5 | % |
| Break,23°C | ISO527-2 | 2.5 | % | |
| Bending modulus | ASTMD790 | 7600 | Mpa | |
| 23°C | ISO178 | 8000 | Mpa | |
| bending strength | ASTMD790 | 216 | Mpa | |
| tensile strength | 干(湿) | ASTM D-638 | 153(123) | Mpa |
| Rockwell hardness | 干(湿) | ASTM D-785 | 95(55) | M Scale |
| Cantilever beam notch impact strength | 干(湿) | ASTM D-256 | 63(72) | J/m |
| Fracture elongation rate | 干(湿) | ASTM D-638 | 2.5(2.7) | % |
| Scratch resistance coefficient | 干(湿) | ASTM D-790 | 7.6(5.9) | GPa |
| bending strength | 23°C | ISO178 | 208 | Mpa |
| Impact strength of simply supported beam without notch | ISO179 | 64 | kJ/m² | |
| Rockwell hardness | M-Scale | ASTMD785 | 95 | |
| M-Scale | ISO2039-2 | 95 | ||
| Flexural strength | 干(湿) | ASTM D-790 | 216(177) | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.82MPa,干 | ASTM D-648 | 248 | °C |
| Flame retardant grade | 干 | UL 94 | V-0 | |
| Hot deformation temperature | 0.46MPa,干 | ASTM D-648 | 255 | °C |
| Linear coefficient of thermal expansion | 干 | ASTM D-696 | 3 | ×10-5/K |
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 255 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 256 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 240 | °C | |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 3E-05 | cm/cm/°C |
| Hot deformation temperature | 1.8MPa,Unannealed | ASTMD648 | 248 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | IEC60243-1 | 28 | KV/mm | |
| Leakage Trace Index | 3.00mm | IEC60112 | 250 | V |
| Surface resistivity | ASTMD257 | 1E+14 | ohms | |
| IEC60093 | 1E+14 | ohms | ||
| Volume resistivity | ASTMD257 | 1E+15 | ohms·cm | |
| 23°C | IEC60093 | 1E+15 | ohms·cm | |
| Dielectric strength | ASTMD149 | 28 | KV/mm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.75mm | UL94 | V-0 | |
| Burning wire flammability index | 3.0mm | IEC60695-2-12 | 960 | °C |
| Extreme Oxygen Index | ASTMD2863 | 37 | % |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen index | 干 | ASTM D-2863 | 37 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.