PA6 Durethan® BKV30H2.0 BK LANXESS GERMANY
317
Unit Price:$3306 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Thermal stability
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Apparent density | ISO60 | 0.60 | g/cm³ | |
| Shrinkage rate | TD:280°C,2.00mm2 | ISO294-4 | 0.81 | % |
| TD:120°C,2hr,2.00mm3 | ISO294-4 | 0.10 | % | |
| MD:280°C,2.00mm2 | ISO294-4 | 0.29 | % | |
| MD:120°C,2hr,2.00mm3 | ISO294-4 | 0.050 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 7.0 | % |
| Equilibrium,23°C,50%RH | ISO62 | 2.1 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ASTMD638 | 8730 | Mpa |
| 23°C | ISO527-2/1 | 9400 | Mpa | |
| tensile strength | Break,23°C | ASTMD638 | 165 | Mpa |
| Cantilever beam without notch impact strength | 23°C | ISO180/1U | 60 | kJ/m² |
| Ball pressure hardness | ISO2039-1 | 193 | Mpa | |
| tensile strength | Break,23°C | ISO527-2/5 | 170 | Mpa |
| elongation | Break,23°C | ASTMD638 | 3.2 | % |
| Break,23°C | ISO527-2/5 | 3.0 | % | |
| Bending modulus | 23°C | ASTMD790 | 8000 | Mpa |
| 23°C | ISO178/A | 8400 | Mpa | |
| bending strength | 23°C | ASTMD790 | 260 | Mpa |
| 3.5%Strain | ISO178/A | 255 | Mpa | |
| 23°C | ISO178 | 260 | Mpa | |
| FlexuralStrainatFlexuralStrength5(23°C) | 3.6 | % | ||
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 55 | kJ/m² |
| 23°C | ISO179/1eU | 65 | kJ/m² | |
| Cantilever beam without notch impact strength | -30°C | ISO180/1U | 55 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 219 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 210 | °C | |
| 8.0MPa,Unannealed | ISO75-2/C | 150 | °C | |
| vicat softening point | ISO306/B120 | 210 | °C | |
| Ball Pressure Test | 210°C | IEC60695-10-2 | Pass | |
| Melting temperature | ISO11357-3 | 221 | °C | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 2E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 1E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 33 | KV/mm |
| Leakage Trace Index | SolutionA | IEC60112 | 400 | V |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Membrane puncture strength | --6 | ISO6603-2 | 2.10 | J |
| --7 | ISO6603-2 | 2.20 | J | |
| Membrane piercing force | --6 | ISO6603-2 | 744 | N |
| --7 | ISO6603-2 | 803 | N |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| BurningBehavior | ISO3795 | passed |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut | ISO1874 | PA6,GHR,10-090,GF30 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.