ABS TAITALAC® 5000M TAIDA TAIWAN
183
Unit Price:$1549 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 19MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity High gloss Impact resistance High gloss hard Impact resistance High rigidity Highlight Moderate impact resistanc
- Application Areas:Household goods Video tape
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 200℃/5.0 kg | ASTM D1238 | 1.8 | g/10 min |
| 220℃/10.0 kg | ASTM D1238 | 20 | g/10 min | |
| Shrinkage rate | MD | ASTM D955 | < 0.40 | % |
| Water absorption rate | Saturation | ASTM D570 | < 0.30 | % |
| Shrinkage rate | MD | ASTMD995 | <0.40 | % |
| Water absorption rate | (23°C,24hr) | ASTMD570 | <0.30 | % |
| Melt mass flow rate | 200℃/5.0Kg | ASTMD1238 | 1.8 | g/10min |
| 220℃/10.0Kg | ASTMD1238 | 20 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | ASTMD785 | 115 | R | |
| tensile strength | 23°C | ASTMD638 | 44 | Mpa |
| Bending modulus | 23℃ | ASTM D790 | 27000 | Mpa |
| bending strength | Yield, 23℃ | ASTM D790 | 77.5 | Mpa |
| Impact strength of cantilever beam gap | 23℃, 3.18 mm | ASTM D256 | 200 | J/m |
| 23℃, 6.35 mm | ASTM D256 | 180 | J/m | |
| Rockwell hardness | R-Scale, 23℃ | ASTM D785 | 115 | |
| tensile strength | Yield, 23℃, 3.18 mm | ASTM D638 | 44.1 | Mpa |
| Break, 23℃, 3.18 mm | ASTM D638 | 37.3 | Mpa | |
| elongation | Break, 23℃, 3.18 mm | ASTM D638 | 30 | % |
| elongation at break | 23°C | ASTMD638 | 30 | % |
| bending strength | 23°C | ASTMD790 | 76 | Mpa |
| Bending modulus | 23°C | ASTMD790 | 2550 | Mpa |
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 220 | J/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.80MPaUnannealed | ASTMD648 | 85 | °C |
| vicat softening point | ASTM1525 | 103 | °C | |
| Hot deformation temperature | 1.8 MPa, Annealed, 12.7 mm | ASTM D648 | 85 | °C |
| vicat softening point | ASTM D1525 | 103 | °C | |
| High arc combustion index | 1.57 mm | UL 746 | 200 | |
| High voltage arc tracing rate | 1.57 mm | UL 746 | 0.00 | mm/min |
| Hot wire ignition | 1.57 mm | UL 746 | 18 | sec |
| Flame retardant grade | 1.59 mm | UL 94 | HB |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistance | ASTMD257 | 1E+22 | Ω.cm | |
| Insulation strength | ASTMD149 | 22 | KV/mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.