ABS CYCOLAC™ MG37EP BK SABIC INNOVATIVE US
220
Unit Price:$2913 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting High impact resistance
- Application Areas:Household goods Plastic connectors Electronic field Electrical field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40to0.60 | % |
| Melt viscosity | 240°C,1000sec^-1 | ASTMD3835 | 217 | Pa·s |
| density | ISO1183 | 1.04 | g/cm³ | |
| ASTMD792 | 1.05 | g/cm³ | ||
| Melt mass flow rate | 230°C/3.8kg | ASTMD1238 | 6.6 | g/10min |
| 220°C/10.0kg | ISO1133 | 22 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| elongation | 断裂 | ASTMD638 | 54 | % |
| 断裂 | ISO527-2/5 | 18 | % | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 35.6 | J |
| Tensile modulus | ASTMD638 | 2480 | Mpa | |
| Bending modulus | 50.0mm跨距 | ASTMD790 | 2810 | Mpa |
| Tensile modulus | ISO527-2/1 | 2720 | Mpa | |
| Bending modulus | ISO178 | 2480 | Mpa | |
| tensile strength | 屈服 | ASTMD638 | 44.0 | Mpa |
| bending strength | ISO178 | 73.2 | Mpa | |
| tensile strength | 屈服 | ISO527-2/5 | 48.0 | Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTMD790 | 90.3 | Mpa |
| tensile strength | 断裂 | ISO527-2/5 | 36.4 | Mpa |
| Impact strength of cantilever beam gap | -40°C | ASTMD256 | 88 | J/m |
| elongation | 屈服 | ISO527-2/5 | 2.0 | % |
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 250 | J/m |
| 23°C | ISO180/1A | 23 | kJ/m² | |
| -40°C | ISO180/1A | 7.0 | kJ/m² | |
| -30°C | ISO180/1A | 8.2 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 88.0 | °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 76.0 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 82.4 | °C | |
| vicat softening point | ISO306/B50 | 94.0 | °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO11359-2 | 6E-05 | cm/cm/°C |
| TD：-40到40°C | ISO11359-2 | 6E-05 | cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.