ABS POLYLAC® PA-758 TAIWAN CHIMEI
1135
Unit Price:$2304 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 497.15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Material Certification
Technical Data Sheet
Material Description
- Material Properties:transparent
- Application Areas:Household goods｜Home appliance components｜Automotive sector
- Color:--
- Grade:Transparent level
Material Certification
TDS
TDS
SVHC
Processing
Statement
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Density / Specific Gravity | -- | ASTMD792 | 1.08 g/cm³ |
| 23°C | ISO1183 | 1.08 g/cm³ | |
| Melt Mass-Flow Rate | 200°C/5.0kg | ASTMD1238,ISO1133 | 3.0 g/10min |
| Modeling Shrinkage | ISO294-4 | 0.30到0.70 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,退火 | ISO75-2/A | 97.0 °C |
| Vicat Softening Temperature | -- | ASTMD15256 | 105 °C |
| -- | ISO306/A50 | 104 °C | |
| -- | ISO306/B50 | 96.0 °C | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 9E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火 | ASTMD648 | 88.0 °C |
| 1.8MPa,未退火 | ISO75-2/A | 77.0 °C | |
| 1.8MPa,退火 | ASTMD648 | 99.0 °C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flame Rating | 1.5mm | UL94 | HB |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural Strength | --5 | ISO178 | 57.0 Mpa |
| Tensile Stress | 屈服 | ISO527-2/50 | 42.0 Mpa |
| 断裂 | ISO527-2/50 | 33.0 Mpa | |
| --3 | ASTMD638 | 39.7 Mpa | |
| Tensile Elongation | 断裂3 | ASTMD638 | 40 % |
| 断裂 | ISO527-2/50 | 40 % | |
| Flexural Modulus | --4 | ASTMD790 | 1900 Mpa |
| --5 | ISO178 | 1900 Mpa | |
| Flexural Strength | --4 | ASTMD790 | 53.9 Mpa |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | R级 | ASTMD785 | 107 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179 | 7.0 kJ/m² |
| 23°C | ISO179 | 14 kJ/m² | |
| Notched Izod Impact Strength | 23°C,3.20mm | ASTMD256 | 150 J/m |
| 23°C,6.40mm | ASTMD256 | 160 J/m | |
| -30°C | ISO180/1A | 7.0 kJ/m² | |
| 23°C | ISO180/1A | 14 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.