ABS Toyolac® 920 TORAY MALAYSIA
1169
Unit Price:$2224 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 512.6MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high strength transparent
- Application Areas:Electronic field Automotive sector Electrical field Electric appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption | 浸入23℃水中24hr | ASTM D-570 | 0.3 | % |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.3 | % | |
| Melt mass flow rate | 220℃/10.0kg | ASTM D-1238 | g/10min | |
| ASTM D1238/ISO 1133 | 19~23 | g/10min | ||
| density | ASTM D792/ISO 1183 | 1.08 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural strength | 23℃ | ASTM D-790 | kg/cm | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 13 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 6 | kg·cm/cm(J/M)ft·lb/in | ||
| yield strength | 23℃ | ASTM D-638 | kg/cm | |
| Tensile strength under yield | 23℃ | ASTM D-638 | % | |
| Tensile strength at break | 23℃ | ASTM D-638 | % | |
| Flexural limit | 23℃ | ASTM D-790 | kg/cm | |
| Fracture strength | 23℃ | ASTM D-638 | kg/cm | |
| tensile strength | ASTM D638/ISO 527 | 490（屈服）380（断裂） | kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 3.5 | % | |
| Rockwell hardness | ASTM D785 | R-115 | ||
| 23℃ | ASTM D-785 | 115 | R | |
| Bending modulus | ASTM D790/ISO 178 | 23500 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 780 | kg/cm²(MPa)[Lb/in²] | |
| impact strength | 12.7×12.7×62.5mm(带韧口)，23℃；0℃；-30℃ | ASTM D-256 | ||
| 3.2×12.7×62.5mm(带韧口)，23℃；0℃；-30℃ | ASTM D-256 | |||
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 30 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility | UL-94 | |||
| Linear coefficient of thermal expansion | ASTM D-696 | |||
| ASTM D696/ISO 11359 | 1.2x10^-4 | mm/mm.℃ | ||
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | 18.56kg/cm | ASTM D-648 | 89 | ℃ |
| ASTM D648/ISO 75 | 89 | ℃（℉） |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 220℃ | ×10 | 插入式粘度计 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.