ABS POLYLAC® PA-747S TAIWAN CHIMEI
286
Unit Price:$2150 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 276.1MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility
- Application Areas:Home appliance components
- Color:--
- Grade:Withdrawal level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | --3 | ASTMD792 | 1.03 | g/cm³ |
| 23°C | ISO1183 | 1.04 | g/cm³ | |
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 0.50 | g/10min |
| Melt Volume-Flow Rate (MVR) | 220°C/10.0kg | ISO1133 | 2.50 | cm3/10min |
| Shrinkage rate | ISO294-4 | 0.40到0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 102 | |
| tensile strength | Yield4 | ASTMD638 | 38.1 | Mpa |
| Yield | ISO527-2/50 | 41.0 | Mpa | |
| Break | ISO527-2/50 | 30.0 | Mpa | |
| elongation | Break4 | ASTMD638 | 40 | % |
| Break | ISO527-2/50 | 25 | % | |
| Bending modulus | --5 | ASTMD790 | 2070 | Mpa |
| --6 | ISO178 | 1700 | Mpa | |
| bending strength | --5 | ASTMD790 | 60.7 | Mpa |
| --6 | ISO178 | 61.0 | Mpa | |
| Charpy Notched Impact Strength | -30°C | ISO179 | 28 | kJ/m² |
| 23°C | ISO179 | 39 | kJ/m² | |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 400 | J/m |
| 23°C,6.40mm | ASTMD256 | 350 | J/m | |
| -30°C | ISO180/1A | 26 | kJ/m² | |
| 23°C | ISO180/1A | 37 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ASTMD648 | 85.0 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 83.0 | °C | |
| 1.8MPa,Annealed | ASTMD648 | 95.0 | °C | |
| 1.8MPa,Annealed | ISO75-2/A | 99.0 | °C | |
| vicat softening point | -- | ASTMD15257 | 103 | °C |
| -- | ISO306/A50 | 106 | °C | |
| -- | ISO306/B50 | 101 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 9.1E-05 | cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.