PC Makrolon® 6557 704206 COVESTRO SHANGHAI
90
Unit Price:$2734 USD/MT
- Packaging Specification:
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Medium viscosity
- Application Areas:Electrical field Electronic field Industrial applications
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | TD | ISO2577 | 0.60to0.80 | % |
| MD | ISO2577 | 0.60to0.80 | % | |
| TD:2.00mm3 | ISO294-4 | 0.70 | % | |
| MD:2.00mm3 | ISO294-4 | 0.65 | % | |
| 吸水率 | 饱和,23°C | ISO62 | 0.30 | % |
| 平衡,23°C,50%RH | ISO62 | 0.12 | % | |
| 熔体体积流动速率 | 300°C/1.2kg | ISO1133 | 10.0 | cm3/10min |
| 熔体质量流动速率 | 300°C/1.2kg | ISO1133 | 10 | g/10min |
| 表观密度 | ISO60 | 0.64 | g/cm³ | |
| 密度 | 23°C | ISO1183 | 1.20 | g/cm³ |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 标称拉伸断裂应变 | 23°C | ISO527-2/50 | >50 | % |
| 简支梁缺口冲击强度 | -30°C,完全断裂 | ISO7391 | 14 | kJ/m² |
| 23°C,局部断裂 | ISO7391 | 70 | kJ/m² | |
| 简支梁无缺口冲击强度 | -60°C | ISO179/1eU | NoBreak | |
| -30°C | ISO179/1eU | NoBreak | ||
| 23°C | ISO179/1eU | NoBreak | ||
| 球压硬度 | ISO2039-1 | 115 | Mpa | |
| TensileCreepModulus | 1hr | ISO899-1 | 2200 | Mpa |
| 拉伸蠕变模量 | 1000hr | ISO899-1 | 1900 | Mpa |
| 拉伸模量 | 23°C | ISO527-2/1 | 2400 | Mpa |
| 拉伸强度 | 屈服,23°C | ISO527-2/50 | 66.0 | Mpa |
| 断裂,23°C | ISO527-2/50 | 70.0 | Mpa | |
| 伸长率 | 屈服,23°C | ISO527-2/50 | 6.1 | % |
| 断裂,23°C | ISO527-2/50 | 130 | % | |
| 弯曲模量 | 23°C | ISO178 | 2400 | Mpa |
| 弯曲强度 | 3.5%Strain,23°C | ISO178 | 75.0 | Mpa |
| 23°C | ISO178 | 99.0 | Mpa | |
| 悬壁梁缺口冲击强度 | -30°C,完全断裂 | ISO7391 | 12 | kJ/m² |
| 23°C,局部断裂 | ISO7391 | 65 | kJ/m² | |
| 多轴向仪器化冲击力峰值 | -30°C | ISO6603-2 | 6300 | N |
| 23°C | ISO6603-2 | 5400 | N | |
| 多轴向仪器化冲击能量 | -30°C | ISO6603-2 | 65.0 | J |
| 23°C | ISO6603-2 | 60.0 | J | |
| 弯曲应变 | 23°C | ISO178 | 7.0 | % |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 玻璃转化温度 | ISO11357-2 | 144 | °C | |
| 导热系数 | 23°C | ISO8302 | 0.20 | W/m/K |
| 维卡软化点 | -- | ISO306/B50 | 143 | °C |
| -- | ISO306/B120 | 144 | °C | |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| RTIStr | 1.5mm | UL746 | 125 | °C |
| RTI Imp | 1.5mm | UL746 | 115 | °C |
| Ball Pressure Test | 135°C | IEC60695-10-2 | Pass | |
| 线性热膨胀系数 | MD：23到55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| 热变形温度 | 0.45MPa,未退火 | ISO75-2/B | 136 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 124 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 相对电容率 | 23°C,100Hz | IEC60250 | 3.10 | |
| 23°C,1MHz | IEC60250 | 3.00 | ||
| 漏电起痕指数 | 解决方案A | IEC60112 | 225 | V |
| 解决方案B | IEC60112 | 125 | V | |
| 耗散因数 | 23°C,100Hz | IEC60250 | 8E-04 | |
| 23°C,1MHz | IEC60250 | 9E-03 | ||
| 介电强度 | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
| 表面电阻率 | IEC60093 | 1E+16 | ohms | |
| 体积电阻率 | 23°C | IEC60093 | 1E+16 | ohms·cm |
| 薄膜 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| WaterVaporTransmissionRate | 23°C,85%RH,100µm | ISO15106-1 | 15 | g/m²/24hr |
| GasPermeation | CarbonDioxide:23°C,25.4µm | ISO2556 | 16900 | cm³/m²/bar/24hr |
| CarbonDioxide:23°C,100.0µm | ISO2556 | 3800 | cm³/m²/bar/24hr | |
| Nitrogen:23°C,25.4µm | ISO2556 | 510 | cm³/m²/bar/24hr | |
| Nitrogen:23°C,100.0µm | ISO2556 | 120 | cm³/m²/bar/24hr | |
| Oxygen:23°C,25.4µm | ISO2556 | 2760 | cm³/m²/bar/24hr | |
| Oxygen:23°C,100.0µm | ISO2556 | 650 | cm³/m²/bar/24hr |
| 光学性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 透光率 | 1000µm | ISO13468-2 | 89.0 | % |
| 2000µm | ISO13468-2 | 89.0 | % | |
| 3000µm | ISO13468-2 | 88.0 | % | |
| 4000µm | ISO13468-2 | 87.0 | % | |
| 折射率 | ISO489 | 1.586 |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL阻燃等级 | 0.75mm,CL | UL94 | V-2 | |
| 1.5mm | UL94 | V-2 | ||
| 3.0mm | UL94 | V-0 | ||
| 灼热丝易燃指数 | 0.75mm | IEC60695-2-12 | 900 | °C |
| 1.5mm | IEC60695-2-12 | 960 | °C | |
| 3.0mm | IEC60695-2-12 | 960 | °C | |
| 燃烧速率-US-FMVSS | >1.00mm | ISO3795 | passed | |
| FlashIgnitionTemperature | ASTMD1929 | 460 | °C | |
| GlowWireTest | 1.50mm | EDFHN60E.02 | 750 | °C |
| 3.00mm | EDFHN60E.02 | 750 | °C | |
| 针焰试验 | MethodF:1.50mm | IEC60695-11-5 | 2.0 | min |
| MethodF:2.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodF:3.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodK:1.50mm | IEC60695-11-5 | 1.0 | min | |
| MethodK:2.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodK:3.00mm | IEC60695-11-5 | 2.0 | min | |
| 极限氧指数 | ISO4589-2 | 36 | % | |
| SelfIgnitionTemperature | ASTMD1929 | 530 | °C | |
| 热灯丝点火温度 | 0.75mm | IEC60695-2-13 | 875 | °C |
| 1.5mm | IEC60695-2-13 | 875 | °C | |
| 3.0mm | IEC60695-2-13 | 900 | °C | |
| ApplicationofFlamefromSmallBurner-MethodKandF | 2.00mm | DIN53438-1,-3 | K1,F1 |
| 补充信息 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISOShortname | ||||
| ElectrolyticalCorrosion | 23°C | IEC60426 | A1 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.