PC IUPILON™ GS2010MKR MITSUBISHI ENGINEERING JAPAN
98
Unit Price:$2549 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Flame retardant enhance Filler: Glass fiber reinf 10% filler by weight
- Application Areas:fibre
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.3 - 0.5 | % | |
| TD:3.20mm | 0.40to0.60 | % | ||
| MD:3.20mm | 0.30to0.50 | % | ||
| Water absorption rate | Saturation,23°C | ISO62 | 0.14 | % |
| Melt Volume-Flow Rate (MVR) | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 10 | g/10min |
| density | ASTM D792/ISO 1183 | 1.27 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 55 | kJ/m² |
| elongation at break | ASTM D638/ISO 527 | 3.4 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 4200 | kg/cm²(MPa)[Lb/in²] | |
| ISO527-2 | 4500 | Mpa | ||
| tensile strength | Break | ISO527-2 | 78.0 | Mpa |
| elongation | Break | ISO527-2 | 2.9 | % |
| Bending modulus | ISO178 | 4000 | Mpa | |
| ASTM D790/ISO 178 | 3500 | kg/cm²(MPa)[Lb/in²] | ||
| bending strength | ASTM D790/ISO 178 | 120 | kg/cm²(MPa)[Lb/in²] | |
| ISO178 | 135 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 4.0E-05 | mm/mm.℃ | |
| MD | ISO11359-2 | 4E-05 | cm/cm/°C | |
| TD | ISO11359-2 | 6.7E-05 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 145 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 140 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the anti leakage trace index | CTI | UL746 | PLC4 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.75mm | UL94 | V-0 |
| Processing conditions | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Mold temperature | 80-120 | °C | ||
| Processing temperature | 270-290 | °C | ||
| 290-310 | °C | |||
| 280-300 | °C | |||
| Dry conditions | 热风干燥 120℃---約4-8小时 | |||
| Screw speed | 50-100 | rpm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.