PC/ABS CYCOLOY™ CY5100-701 SABIC INNOVATIVE NANSHA
120
Unit Price:$3650 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Ultra high melting finger Aging resistance
- Application Areas:Shell Electronic and electrical
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.40-0.60 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.60 | % | |
| Melt mass flow rate | ASTM D1238/ISO 1133 | 260℃/2.16kg,1.40 | g/10min | |
| density | ASTM D792/ISO 1183 | 1.18 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 缺口：7.5，无缺口：19 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 缺口：1.5, 无缺口：4.8 | kg·cm/cm(J/M)ft·lb/in | ||
| Tensile modulus | ASTM D638/ISO 527 | 400000(399000) | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 9270(6890)/9150(6730) | kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 4.1/4.0 | % | |
| Bending modulus | ASTM D790/ISO 178 | 354000 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 13700 | kg/cm²(MPa)[Lb/in²] | |
| Charpy impact strength | ASTM D256/ISO 179 | 1/6" 23℃ 缺口：4.8，无缺口：19 | kg·cm/cm(J/M)ft·lb/in | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 65/35 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 0.000044 | mm/mm.℃ | |
| Combustibility (rate) | UL94 | V1-V0 | ||
| vicat softening point | ASTM D1525/ISO R306 | 220-223 | ℃（℉） | |
| Hot deformation temperature | ASTM D648/ISO 75 | 191 | ℃（℉） |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTM D257/IEC 60093 | 1.0E+15 ohm.cm | Ω | |
| Dielectric constant | ASTM D150/IEC 60250 | 50HZ/60HZ:2.90 | ||
| ASTM D150/IEC 60250 | 2.90 | |||
| Volume resistivity | ASTM D257/IEC 60093 | 1.0E+15 ohms | Ω.cm |
| Processing conditions | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dry conditions | 干燥温度：176-194℉,干燥时间:2.0-4.0hr | |||
| Melt Temperature | 482-572 | °C | ||
| Processing temperature | 446-536 | °C | ||
| 482-572 | °C | |||
| 464-554 | °C | |||
| Mold temperature | 140-185 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.