PC/ABS CYCOLOY™ CX7240U-7M10001 SABIC INNOVATIVE SINGAPHORE
121
Unit Price:$3868 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant High impact resistance High mobility
- Application Areas:Electrical field Electronic field Architectural application Outdoor applications Engine hood parts Medical supplies Nursing supplies Plastic bag Casters Aerospace Applications Liquid handling
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 260°C/2.16 kg | ASTM D1238 | 16 | g/10 min |
| Melt Volume-Flow Rate (MVR) | 260°C/2.16 kg | ISO 1133 | 15.0 | cm3/10min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.40 到 0.60 | % |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.20 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.10 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -- 2 | ASTM D638 | 2950 | Mpa |
| -- | ISO 527-2/1 | 2530 | Mpa | |
| tensile strength | Yield 3 | ASTM D638 | 65.0 | Mpa |
| Yield | ISO 527-2/50 | 65.0 | Mpa | |
| Break 3 | ASTM D638 | 58.0 | Mpa | |
| Break | ISO 527-2/50 | 50.0 | Mpa | |
| elongation | Yield 3 | ASTM D638 | 4.1 | % |
| Yield | ISO 527-2/50 | 4.0 | % | |
| Break 3 | ASTM D638 | 100 | % | |
| Break | ISO 527-2/50 | 90 | % | |
| Bending modulus | 50.0 mm Span 4 | ASTM D790 | 2750 | Mpa |
| -- 5 | ISO 178 | 2500 | Mpa | |
| bending strength | -- 5, 6 | ISO 178 | 96.0 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 104 | Mpa | |
| Impact strength of simply supported beam gap | -30°C | ISO 179/1eA | 10 | kJ/m² |
| 23°C | ISO 179/1eA | 20 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 65.0 | J |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 100 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 89.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 99.0 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9 | ISO 75-2/Af | 93.0 | °C | |
| vicat softening point | -- | ASTM D152510 | 106 | °C |
| -- | ISO 306/B50 | 110 | °C | |
| -- | ISO 306/B120 | 113 | °C | |
| Ball Pressure Test | 73 to 77°C | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 6.3E-5 | cm/cm/°C |
| Flow : -40 to 40°C | ISO 11359-2 | 6.2E-5 | cm/cm/°C | |
| Across Flow : -40 to 40°C | ASTM E831 | 5.4E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 5.4E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | 90.0 | °C | |
| RTI Imp | UL 746 | 90.0 | °C | |
| RTI | UL 746 | 90.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | ||
| High arc combustion index (HAI) | UL 746 | PLC 0 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 3 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 90 | °C | ||
| drying time | 4.0 | hr | ||
| Suggested maximum moisture content | 0.040 | % | ||
| Suggested injection volume | 40 到 80 | % | ||
| Hopper temperature | 60 到 80 | °C | ||
| Temperature at the rear of the barrel | 260 到 300 | °C | ||
| Temperature in the middle of the barrel | 260 到 300 | °C | ||
| Temperature at the front of the material cylinder | 265 到 300 | °C | ||
| Spray nozzle temperature | 265 到 300 | °C | ||
| Processing (melt) temperature | 270 到 300 | °C | ||
| Mold temperature | 60 到 90 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 40 到 70 | rpm | ||
| Exhaust hole depth | 0.038 到 0.076 | mm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.40 mm | UL 94 | V-2 | |
| 0.60 mm | UL 94 | V-1 | ||
| 0.75 mm | UL 94 | V-0 | ||
| 1.5 mm | UL 94 | 5VB | ||
| 3.0 mm | UL 94 | 5VA | ||
| Burning wire flammability index | 0.75 mm | IEC 60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.0 mm | IEC 60695-2-13 | 825 | °C |
| 3.0 mm | IEC 60695-2-13 | 800 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.