PBT VALOX™ ENH4560 BK1066 SABIC INNOVATIVE SHANGHAI
123
Unit Price:$7164 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Bromine free Chlorine free
- Application Areas:Plastic bag Automotive External Parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume-Flow Rate (MVR) | 250°C/5.0kg | ISO1133 | 16.0 | cm3/10min |
| Melt mass flow rate | 265°C/5.0kg | ASTMD1238 | 23 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 23°C | ASTMD4812 | 500 | J/m | |
| ASTMD256 | 75 | J/m | ||
| 0°C | ASTMD256 | 75 | J/m | |
| Surrender | ASTMD638 | 110 | Mpa | |
| Fracture | ASTMD638 | 110 | Mpa | |
| Yield, 50.0mm span | ASTMD790 | 150 | Mpa | |
| -30°C | ISO180/1A | 9.0 | kJ/m² | |
| ASTMD256 | 75 | J/m | ||
| ASTMD4812 | 500 | J/m | ||
| ISO180/1U | 37 | kJ/m² | ||
| 23°C | ISO180/1A | 9.0 | kJ/m² | |
| ISO180/1U | 37 | kJ/m² | ||
| 0°C | ISO180/1A | 9.0 | kJ/m² | |
| Fracture, 50.0mm span of | ASTMD790 | 150 | Mpa | |
| Fracture bending strain | ISO178 | 2.0 | % | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/2U | 35 | kJ/m² |
| 23°C | ISO179/2U | 40 | kJ/m² | |
| Ball pressure hardness | H358/30 | ISO2039-1 | 142 | Mpa |
| Rockwell hardness | R-Sale | ISO2039-2 | 120 | |
| yield | ISO527-2/5 | 105 | Mpa | |
| ISO527-2/5 | 2.0 | % | ||
| crack | ISO527-2/5 | 105 | Mpa | |
| ISO527-2/5 | 2.0 | % | ||
| 50.0mm span | ASTMD790 | 9000 | Mpa | |
| -- | ISO178 | 10000 | Mpa | |
| ISO178 | 170 | Mpa | ||
| ASTMD638 | 11000 | Mpa | ||
| Surrender | ASTMD638 | 2.0 | % | |
| Fracture | ASTMD638 | 2.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTI Imp | UL746 | 125 | °C | |
| Linear coefficient of thermal expansion | MD:-40to40°C | ISO11359-2 | 2E-05 | cm/cm/°C |
| MD:23to150°C | ISO11359-2 | 2.5E-05 | cm/cm/°C | |
| TD:-40to40°C | ISO11359-2 | 6.2E-05 | cm/cm/°C | |
| TD:23to150°C | ISO11359-2 | 1.5E-04 | cm/cm/°C | |
| RTI | UL746 | 140 | °C | |
| RTIElec | UL746 | 140 | °C | |
| 0.45MPa, unannealed, 64.0mm span | ISO75-2/Bf | 225224 | °C | |
| 1.8MPa, unannealed, 64.0mm span | ISO75-2/Af | 210 | °C | |
| Ball Pressure Test | 125°C | IEC60695-10-2 | Pass | |
| 0.45MPa, unannealed, 3.20mm | ASTMD648 | 223 | °C | |
| -- | ASTMD152520 | 217 | °C | |
| ISO306/A50 | 220 | °C | ||
| ISO306/B50 | 206 | °C | ||
| ISO306/B120 | 205 | °C | ||
| ASTMD152519 | 207 | °C | ||
| 1.8MPa, unannealed, 3.20mm | ASTMD648 | 210 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 1.60mm,inOil | ASTMD149 | 22 | KV/mm | |
| 3.20mm, inoil | ASTMD149 | 18 | KV/mm | |
| 0.800mm, in oil | IEC60243-1 | 32 | KV/mm | |
| 1.60mm, in oil | IEC60243-1 | 22 | KV/mm | |
| 3.20mm, in oil | IEC60243-1 | 18 | KV/mm | |
| 0.800mm,inOil | ASTMD149 | 32 | KV/mm | |
| Dissipation factor | 1MHz | ASTMD150,IEC60250 | 0.14 | |
| Leakage Trace Index | IEC60112 | 600 | V | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC0 | |
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Dielectric constant | 1MHz | ASTMD150,IEC60250 | 3.80 | |
| Volume resistivity | ASTMD257,IEC60093 | 1E+14 | ohms·cm | |
| Hot wire ignition | HWI | UL746 | PLC0 | |
| High arc combustion index | HAI | UL746 | PLC0 |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 260°C,1500sec^-1 | ISO11443 | 110 | Pa·s |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.800mm | UL94 | V-0 | |
| 3.00mm | UL94 | 5VB | ||
| Burning wire flammability index | 2.00mm | IEC60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 2.00mm | IEC60695-2-13 | 750 | °C |
| 3.00mm | IEC60695-2-13 | 800 | °C | |
| 1.00mm | IEC60695-2-13 | 750 | °C |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Filling material | ASTMD229 | 30 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.