PBT VALOX™ V4860HR BK1066 SABIC INNOVATIVE JAPAN
175
Unit Price:$9265 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Dimensional stability
- Application Areas:Automotive Applications Casters
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTMD792 | 1.64 | g/cm³ | |
| ISO1183 | 1.64 | g/cm³ | ||
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.060 | % |
| Saturation,23°C | ISO62 | 0.19 | % | |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.50to1.0 | % |
| MD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| Melt Volume-Flow Rate (MVR) | 250°C/5.0kg | ISO1133 | 12.4 | cm3/10min |
| Melt mass flow rate | 250°C/5.0kg | ASTMD1238 | 18 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | Break | ISO527-2/5 | 111 | Mpa |
| elongation | Yield | ASTMD638 | 2.3 | % |
| Yield | ISO527-2/5 | 2.1 | % | |
| Break | ASTMD638 | 2.3 | % | |
| Break | ISO527-2/5 | 2.2 | % | |
| Bending modulus | 50.0mmSpan | ASTMD790 | 6740 | Mpa |
| ISO178 | 7880 | Mpa | ||
| bending strength | --6 | ISO178 | 182 | Mpa |
| --7 | ISO178 | 183 | Mpa | |
| tensile strength | Break | ASTMD638 | 115 | Mpa |
| Yield | ISO527-2/5 | 112 | Mpa | |
| Yield | ASTMD638 | 116 | Mpa | |
| Tensile modulus | ISO527-2/1 | 9450 | Mpa | |
| ASTMD638 | 9750 | Mpa | ||
| bending strength | Yield,50.0mmSpan | ASTMD790 | 174 | Mpa |
| Break,50.0mmSpan | ASTMD790 | 2.96 | Mpa | |
| Fracture bending strain | ISO178 | 2.9 | % | |
| CharpyNotchedImpactStrength | 23°C | ISO179/1eA | 11 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 74 | J/m |
| 23°C | ASTMD256 | 90 | J/m | |
| -30°C | ISO180/1A | 8.5 | kJ/m² | |
| 23°C | ISO180/1A | 10 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 13.4 | J |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 221 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 197 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 205 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 188 | °C | |
| vicat softening point | ASTMD152512 | 176 | °C | |
| -- | ISO306/B50 | 176 | °C | |
| -- | ISO306/B120 | 175 | °C | |
| BallPressureTest | 75°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40to95°C | ASTME831 | 2.4E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 2.3E-05 | cm/cm/°C | |
| TD：-40to95°C | ASTME831 | 1.1E-04 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 1.2E-04 | cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.8mm,TestingbySABIC | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.