PC LEXAN™ EXL9414T-1T9A8054T SABIC INNOVATIVE NANSHA
98
Unit Price:$3938 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Low temperature and high
- Application Areas:Thin walled products
- Color:--
- Grade:--
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 熔体质量流动速率 | 300°C/1.2 kg | ASTM D1238 | 13 | g/10 min |
| 熔体体积流动速率 | 300°C/1.2 kg | ISO 1133 | 12.0 | cm3/10min |
| 收缩率 - 流动 | 3.20 mm | 内部方法 | 0.40 到 0.80 | % |
| 吸水率 | 饱和, 23°C | ISO 62 | 0.12 | % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.090 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 拉伸模量 | -- 1 | ASTM D638 | 2180 | Mpa |
| -- | ISO 527-2/1 | 2300 | Mpa | |
| 拉伸强度 | 屈服 2 | ASTM D638 | 57.0 | Mpa |
| 屈服 | ISO 527-2/50 | 56.0 | Mpa | |
| 断裂 2 | ASTM D638 | 59.0 | Mpa | |
| 断裂 | ISO 527-2/50 | 55.0 | Mpa | |
| 伸长率 | 屈服 2 | ASTM D638 | 5.6 | % |
| 屈服 | ISO 527-2/50 | 5.4 | % | |
| 断裂 2 | ASTM D638 | 120 | % | |
| 断裂 | ISO 527-2/50 | 110 | % | |
| 弯曲模量 | 50.0 mm 跨距 3 | ASTM D790 | 2180 | Mpa |
| -- 4 | ISO 178 | 2120 | Mpa | |
| 弯曲强度 | -- 4, 5 | ISO 178 | 88.0 | Mpa |
| 屈服, 50.0 mm 跨距 3 | ASTM D790 | 92.0 | Mpa | |
| 简支梁缺口冲击强度 | -30°C | ISO 179/1eA | 60 | kJ/m² |
| 23°C | ISO 179/1eA | 70 | kJ/m² | |
| 简支梁无缺口冲击强度 | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| 无缺口伊佐德冲击强度 | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 | ||
| 装有测量仪表的落镖冲击 | 23°C, Total Energy | ASTM D3763 | 75.0 | J |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 120 | °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8 | ISO 75-2/Af | 116 | °C | |
| 维卡软化点 | -- | ASTM D15259, ISO 306/B509 | 138 | °C |
| -- | ISO 306/B120 | 139 | °C | |
| 线性热膨胀系数 | 流动 : -40 到 95°C | ASTM E831 | 6.7E-5 | cm/cm/°C |
| 流动 : 23 到 80°C | ISO 11359-2 | 6.7E-5 | cm/cm/°C | |
| 横向 : -40 到 95°C | ASTM E831 | 8.0E-5 | cm/cm/°C | |
| 横向 : 23 到 80°C | ISO 11359-2 | 8.0E-5 | cm/cm/°C |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 120 | °C | ||
| 干燥时间 | 3.0 到 4.0 | hr | ||
| 建议的最大水分含量 | 0.020 | % | ||
| 建议注射量 | 40 到 60 | % | ||
| 料筒后部温度 | 270 到 295 | °C | ||
| 料筒中部温度 | 280 到 305 | °C | ||
| 料筒前部温度 | 295 到 315 | °C | ||
| 射嘴温度 | 290 到 310 | °C | ||
| 加工（熔体）温度 | 295 到 315 | °C | ||
| 模具温度 | 70 到 95 | °C | ||
| 背压 | 0.300 到 0.700 | Mpa | ||
| 螺杆转速 | 40 到 70 | rpm | ||
| 排气孔深度 | 0.025 到 0.076 | mm |
| 光学性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 透光率 | 2000 µm | 内部方法 | 84.0 | % |
| 雾度 | 2000 µm | 内部方法 | 3.0 | % |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL 阻燃等级 | 1.5 mm | UL 94 | V-1 | |
| 1.8 mm | UL 94 | V-0 | ||
| 极限氧指数 | ISO 4589-2 | 35 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.