PBT VALOX™ 310SEO-1001 SABIC INNOVATIVE JAPAN
183
Unit Price:$4354 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant
- Application Areas:Industrial applications Electrical field Electronic field Switch panel Shell currency
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 特定体积 | ASTM D792 | 0.710 | cm³/g | |
| 熔体质量流动速率 | 250°C/2.16 kg | ASTM D1238 | 8.6 | g/10 min |
| 熔体体积流动速率 | 250°C/2.16 kg | ISO 1133 | 8.00 | cm3/10min |
| 收缩率 | 流动 2 | 内部方法 | 1.1 到 1.8 | % |
| 流动 : 0.750 到 2.30 mm | 内部方法 | 0.90 到 1.6 | % | |
| 流动 : 3.20 mm | 内部方法 | 1.5 到 2.3 | % | |
| 流动 : 2.30 到 4.60 mm | 内部方法 | 1.5 到 2.3 | % | |
| 横向流动 2 | 内部方法 | 0.90 到 1.9 | % | |
| 横向流动 : 0.750 到 2.30 mm | 内部方法 | 1.0 到 1.7 | % | |
| 横向流动 : 2.30 到 4.60 mm | 内部方法 | 1.6 到 2.4 | % | |
| 吸水率 | 饱和, 23°C | ISO 62 | 0.36 | % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.080 | % | |
| 特定体积 | ASTMD792 | 0.770 | cm³/g | |
| 收缩率 | MD：--2 | 内部方法 | 0.90to1.6 | % |
| MD：--3 | 内部方法 | 1.5to2.3 | % | |
| TD：--2 | 内部方法 | 1.0to1.7 | % | |
| TD：--3 | 内部方法 | 1.6to2.4 | % | |
| 吸水率 | 24hr | ASTMD570 | 0.080 | % |
| 熔体粘度 | 内部方法 | 600 | Pa·s |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 弯曲模量 | 50.0mmSpan | ASTMD790 | 2340 | Mpa |
| FlexuralStrength | Yield,50.0mmSpan | ASTMD790 | 82.7 | Mpa |
| Break,50.0mmSpan | ASTMD790 | 82.7 | Mpa | |
| 落锤冲击 | 23°C | ASTMD3029 | 40.7 | J |
| 23°C6 | ASTMD3029 | 40.7 | J | |
| 洛氏硬度 | R级 | ASTMD785 | 117 | |
| 抗张强度 | 屈服 | ASTMD638 | 51.7 | Mpa |
| 拉伸强度 | Break | ASTMD638 | 51.7 | Mpa |
| 伸长率 | 断裂 | ASTMD638 | 300 | % |
| 洛氏硬度 | R 计秤 | ISO 2039-2 | 120 | |
| 球压硬度 | H 358/30 | ISO 2039-1 | 105 | Mpa |
| 拉伸模量 | -- 3 | ASTM D638 | 2820 | Mpa |
| -- | ISO 527-2/1 | 2800 | Mpa | |
| 拉伸强度 | 屈服 4 | ASTM D638 | 58.0 | Mpa |
| 屈服 | ISO 527-2/50 | 58.0 | Mpa | |
| 断裂 4 | ASTM D638 | 52.0 | Mpa | |
| 断裂 | ISO 527-2/50 | 40.0 | Mpa | |
| 伸长率 | 屈服 4 | ASTM D638 | 5.0 | % |
| 屈服 | ISO 527-2/50 | 5.0 | % | |
| 断裂 4 | ASTM D638 | 18 | % | |
| 断裂 | ISO 527-2/50 | 18 | % | |
| 弯曲模量 | 50.0 mm 跨距 5 | ASTM D790 | 2620 | Mpa |
| -- 6 | ISO 178 | 2600 | Mpa | |
| 弯曲强度 | -- 6, 7 | ISO 178 | 90.0 | Mpa |
| 屈服, 50.0 mm 跨距 5 | ASTM D790 | 101 | Mpa | |
| 泰伯耐磨性 | 1000 Cycles, 1000 g, CS-17 转轮 | 内部方法 | 19.0 | mg |
| 简支梁无缺口冲击强度 | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| 无缺口悬臂梁冲击 | 23°C | ASTM D4812, ISO 180/1U | 无断裂 | |
| -30°C 9 | ISO 180/1U | 无断裂 | ||
| 装有测量仪表的落镖冲击 | 23°C, Total Energy | ASTM D3763 | 200 | J |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 162 | °C |
| 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 10 | ISO 75-2/Be | 150 | °C | |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 74.0 | °C | |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 71.0 | °C | |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 10 | ISO 75-2/Ae | 60.0 | °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9 | ISO 75-2/Af | 73.0 | °C | |
| 维卡软化点 | -- | ASTM D152511, ISO 306/B50, ISO 306/B120 | 170 | °C |
| -- | ISO 306/A50 | 212 | °C | |
| Ball Pressure Test | 123 到 127°C | IEC 60695-10-2 | 通过 | |
| 线性热膨胀系数 | 流动 : -40 到 40°C | ASTM E831 | 7.9E-5 | cm/cm/°C |
| 流动 : 60 到 138°C | ASTM E831 | 1.3E-4 | cm/cm/°C | |
| 流动 : -40 到 40°C | ISO 11359-2 | 7.6E-5 | cm/cm/°C | |
| 流动 : 23 到 60°C | ISO 11359-2 | 1.0E-4 | cm/cm/°C | |
| 横向 : -40 到 40°C | ASTM E831 | 7.9E-5 | cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 7.3E-5 | cm/cm/°C | |
| 横向 : 23 到 60°C | ISO 11359-2 | 1.0E-4 | cm/cm/°C | |
| 导热系数 | ISO 8302 | 0.24 | W/m/K | |
| RTI Elec | UL 746 | 120 | °C | |
| RTI Imp | UL 746 | 120 | °C | |
| RTI | UL 746 | 140 | °C | |
| 热变形温度 | 0.45MPa,未退火,6.40mm | ASTMD648 | 154 | °C |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 54.4 | °C | |
| 线性热膨胀系数 | MD：-40to40°C | ASTME831 | 8.1E-05 | cm/cm/°C |
| MD：60to138°C | ASTME831 | 1.4E-04 | cm/cm/°C | |
| RTIElec | UL746 | 120 | °C | |
| RTI Imp | UL746 | 120 | °C | |
| RTIStr | UL746 | 140 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 体积电阻率 | ASTMD257 | >4.0E+16 | ohms·cm | |
| 介电强度 | 1.60mm,inAir | ASTMD149 | 23 | KV/mm |
| 1.60mm,在油中 | ASTMD149 | 23 | KV/mm | |
| 3.20mm,inAir | ASTMD149 | 16 | KV/mm | |
| 3.20mm,在油中 | ASTMD149 | 16 | KV/mm | |
| 介电常数 | 100Hz | ASTMD150 | 3.30 | |
| 1MHz | ASTMD150 | 3.10 | ||
| 耗散因数 | 100Hz | ASTMD150 | 2E-03 | |
| 1MHz | ASTMD150 | 0.020 | ||
| 耐电弧性 | ASTMD495 | PLC5 | ||
| 相比耐漏电起痕指数 | CTI | UL746 | PLC0 | |
| 高电压电弧起痕速率 | HVTR | UL746 | PLC1 | |
| 表面电阻率 | IEC 60093 | > 1.0E+15 | ohms | |
| 体积电阻率 | IEC 60093 | > 1.0E+15 | ohms·cm | |
| 介电强度 | 1.60 mm, in Oil | ASTM D149 | 24 | KV/mm |
| 3.20 mm, in Air | ASTM D149 | 18 | KV/mm | |
| 0.800 mm, 在油中 | IEC 60243-1 | 35 | KV/mm | |
| 1.00 mm 12 | IEC 60243-1 | 18 | KV/mm | |
| 1.60 mm, 在油中 | IEC 60243-1 | 25 | KV/mm | |
| 3.20 mm, 在油中 | IEC 60243-1 | 17 | KV/mm | |
| 相对电容率 | 50 Hz | IEC 60250 | 2.90 | |
| 60 Hz | IEC 60250 | 2.90 | ||
| 100 Hz | IEC 60250 | 3.10 | ||
| 1 MHz | IEC 60250 | 2.80 | ||
| 耗散因数 | 50 Hz | IEC 60250 | 1.0E-3 | |
| 60 Hz | IEC 60250 | 1.0E-3 | ||
| 100 Hz | IEC 60250 | 2.0E-3 | ||
| 1 MHz | IEC 60250 | 0.013 | ||
| 耐电弧性 | ASTM D495 | PLC 6 | ||
| 相比耐漏电起痕指数(CTI) | UL 746 | PLC 3 | ||
| 漏电起痕指数 | -- | IEC 60112 | 175 | V |
| 解决方案 B | IEC 60112 | 100 | V | |
| 高电弧燃烧指数(HAI) | UL 746 | PLC 0 | ||
| 高压电弧抗点燃指数 (HVAR) (PLC) | UL 746 | PLC 6 | ||
| 高电压电弧起痕速率 (HVTR) | UL 746 | PLC 4 | ||
| 热丝引燃 (HWI) | UL 746 | PLC 2 |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 120 | °C | ||
| 干燥时间 | 3.0 到 4.0 | hr | ||
| 建议的最大水分含量 | 0.020 | % | ||
| 建议注射量 | 40 到 80 | % | ||
| 料筒后部温度 | 230 到 250 | °C | ||
| 料筒中部温度 | 240 到 255 | °C | ||
| 料筒前部温度 | 245 到 260 | °C | ||
| 射嘴温度 | 240 到 255 | °C | ||
| 加工（熔体）温度 | 245 到 260 | °C | ||
| 模具温度 | 50 到 75 | °C | ||
| 背压 | 0.300 到 0.700 | Mpa | ||
| 螺杆转速 | 50 到 100 | rpm | ||
| 排气孔深度 | 0.013 到 0.025 | mm |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL 阻燃等级 | 0.71 mm | UL 94 | V-0 | |
| 3.0 mm | UL 94 | 5VA | ||
| 灼热丝易燃指数 | 1.0 mm | IEC 60695-2-12 | 960 | °C |
| 极限氧指数 | ISO 4589-2 | 30 | % | |
| UL阻燃等级 | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.