Material Description
Technical Data Sheet
Material Description
- Material Properties:Ultra high impact resista Widely used for extrusion Ultra high impact strengt Good processability Excellent hot forming
- Application Areas:Used for luggage Toolbox Locomotive parts Low temperature products Helmet Bus box heel Controlled pipe fittings Application in the automo Footwear
- Color:--
- Grade:Heat resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 200℃/5kg | ASTM D-1238 | 0.8 | g/10min |
| 200℃/5kg | ASTM D-1238 | 8.0 | g/10min | |
| Density/specific gravity | ASTM D-792 | 1.03 | ||
| Water absorption rate | ASTM D-570 | 0.3 | wt% | |
| Shrinkage rate | ASTM D-955 | 0.4 | % | |
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 0.80 | g/10min |
| 220°C/10.0kg | ASTMD1238 | 8.0 | g/10min | |
| Shrinkage rate | MD | ASTMD955 | <0.40 | % |
| density | ASTMD792 | 1.03 | g/cm³ | |
| Water absorption rate | 24hr | ASTMD570 | <0.30 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale,23°C | ASTMD785 | 100 | |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTMD256 | 450 | J/m |
| 23°C,3.18mm | ASTMD256 | 490 | J/m | |
| bending strength | Yield,23°C | ASTMD790 | 58.6 | Mpa |
| Bending modulus | 23°C | ASTMD790 | 2000 | Mpa |
| elongation | Break,23°C,3.18mm | ASTMD638 | 90 | % |
| Tensile strength | Break,23°C,3.18mm | ASTMD638 | 27.6 | Mpa |
| Yield,23°C,3.18mm | ASTMD638 | 32.4 | Mpa | |
| Impact strength of cantilever beam gap | 23℃1/2" | ASTM D-256 | 38 (7.0) | kg.cm/cm(ft.1b/in) |
| 23℃1/8" | ASTM D-256 | 53 (9.8) | kg.cm/cm(ft.1b/in) | |
| Tensile strength at the point of surrender | 23℃ | ASTM D-638 | 350 | kg/cm |
| 23℃ | ASTM D-638 | 5000 | psi | |
| Tensile strength at fracture point | 1/8" | ASTM D-638 | 4300 | kg/cm |
| 1/8" | ASTM D-638 | 300 | psi | |
| elongation at break | 1/8" | ASTM D-638 | 50 | % |
| Flexural strength | 23℃ 2.8mm/min | ASTM D-790 | 600 | kg/cm |
| 23℃ 2.8mm/min | ASTM D-790 | 8500 | psi | |
| Flexural coefficient | 23℃ 2.8mm/min | ASTM D-790 | 20000 | kg/cm |
| 23℃ 2.8mm/min | ASTM D-790 | 290000 | psi | |
| Rockwell hardness | 100 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | Unannealed | ASTM D-1525 | 85(185) | ℃(F) |
| vicat softening point | ASTM D-1525 | 100 | °C | |
| Flame retardant grade | UL94 | HB | ||
| Hot deformation temperature | 1.8MPa,Unannealed,12.7mm | ASTMD648 | 85.0 | °C |
| vicat softening point | ASTMD15254 | 102 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 1.6mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.