PA66 FR7026V0FNC010 DUPONT SHENZHEN
143
Unit Price:$6807 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow | ISO 294-4 | 1.0 | % |
| 流量 | ISO 294-4 | 0.90 | % | |
| Water absorption rate | Saturation, 23°C, 2.00 mm | ISO 62 | 8.0 | % |
| Equilibrium, 23°C, 2.00 mm, 50% RH | ISO 62 | 2.4 | % | |
| Stickiness number | ISO 307 | 160 | cm³/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | H 358/30 | ISO 2039-1 | -- | Mpa |
| Tensile modulus | ISO 527-2 | 3800 | Mpa | |
| tensile strength | Yield | ISO 527-2 | -- | Mpa |
| Break | ISO 527-2 | 80.0 | Mpa | |
| elongation | Yield | ISO 527-2 | -- | % |
| Break | ISO 527-2 | 10 | % | |
| Nominal tensile fracture strain | ISO 527-2 | -- | % | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 80 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 230 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 80.0 | °C | |
| Melting temperature | ISO 11357-3 | 260 | °C | |
| Ball Pressure Test | IEC 60309-1 | 220 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 62631-3-2 | -- | ohms | |
| Dielectric strength | IEC 60243-1 | 31 | KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 0 | ||
| Leakage Trace Index | IEC 60112 | 600 | V |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt density | 1.03 | g/cm³ | ||
| Top out temperature | 210 | °C | ||
| Specific Heat Capacity of Melt | 2590 | J/kg/°C | ||
| Thermal Conductivity of Melt | 0.17 | W/m/K | ||
| Odor | VDA 270 | 5.00 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 | °C | ||
| Drying time - hot air dryer | 2.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.20 | % | ||
| Processing (melt) temperature | 270 到 290 | °C | ||
| Melt Temperature, Optimum | 280 | °C | ||
| Mold temperature | 50 到 90 | °C | ||
| Mold Temperature, Optimum | 70 | °C | ||
| Maintain pressure | 50.0 到 100 | Mpa | ||
| Drying Recommended | yes | |||
| Hold Pressure Time | 3.00 | s/mm | ||
| Maximum Screw Tangential Speed | 12 | m/min |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8 mm | UL 94, IEC 60695-11-10, -20 | V-0 | |
| 1.5 mm | UL 94, IEC 60695-11-10, -20 | V-0 | ||
| Burning wire flammability index | 0.40 mm | IEC 60695-2-12 | 960 | °C |
| 0.75 mm | IEC 60695-2-12 | 960 | °C | |
| 1.5 mm | IEC 60695-2-12 | 960 | °C | |
| 3.0 mm | IEC 60695-2-12 | 960 | °C | |
| Hot filament ignition temperature | 0.40 mm | IEC 60695-2-13 | 960 | °C |
| 0.75 mm | IEC 60695-2-13 | 960 | °C | |
| 1.5 mm | IEC 60695-2-13 | 960 | °C | |
| 3.0 mm | IEC 60695-2-13 | 960 | °C | |
| Extreme Oxygen Index | ISO 4589-2 | 39 | % | |
| FMVSS flammability | FMVSS 302 | DNI |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.