PP ExxonMobil™ PP3295G1 EXXONMOBIL USA
164
Unit Price:$1522 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Dimensional stability Easy to color High impact
- Application Areas:chip Automotive sector Seals Non-woven fabric Industrial applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume-Flow Rate (MVR) | 230°C/2.16kg | ISO 527-2/5, ISO 527-2/50 | 0.01到0.07 | |
| 23℃ | g/cm³ | 0.969到1.25 | ||
| % | 0.87到1.2 | |||
| 23℃,24hr | % | 0.020到0.052 | ||
| Flow: 23 ℃ | mm/mm | 139.7E-3到0.432 | ||
| 230°C/2.16kg | g/10min | 0.95到20 | ||
| Lateral flow: 23 ℃ | mm/mm | 0.279到0.457 | ||
| 230°C/2.16kg | g/10min | 4.9到21 | ||
| 23℃,24hr | % | 0.030到0.050 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | MPa | 74.48到85.52 | ||
| 23℃ | 63到78 | |||
| 72到79 | ||||
| Rockwell hardness | 23℃ | 84到106 | ||
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 2.229到8.821 | |
| 23℃ | kJ/m² | 1.858到2.089 | ||
| Falling hammer impact | 23℃ | N.m | 8.85到80.35 | |
| 23℃ | J/m | 0.070到0.203 | ||
| kJ/m² | 0.442到1.347 | |||
| J/m | 0.007到0.013 | |||
| Falling hammer impact | 23℃ | N.m | 26.55到73.89 | |
| Yield, 23 ℃ | % | 2.6到7.2 | ||
| 23℃ | MPa | 1979.31到4220.69 | ||
| MPa | 44.76到50.62 | |||
| Fracture, 23 ℃ | MPa | 44.76到59.03 | ||
| 23℃ | MPa | 33.79到62.48 | ||
| Fracture, 23 ℃ | % | 2.0到31 | ||
| Yield, 23 ℃ | MPa | 28.41到36.76 | ||
| Fracture, 23 ℃ | MPa | 19.03到32.83 | ||
| 23℃ | MPa | 1875.86到4324.14 | ||
| MPa | 30.0到35.52 | |||
| MPa | 1400.0到4703.45 | |||
| Yield, 23 ℃ | MPa | 51.38到55.59 | ||
| MPa | 27.93到35.24 | |||
| Fracture, 23 ℃ | MPa | 21.72到30.28 | ||
| Yield, 23 ℃ | % | 1.7到8.4 | ||
| Fracture, 23 ℃ | % | 3.7到31 | ||
| 23℃ | MPa | 1841.38到4220.69 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 1.8MPa, unannealed | °C | 59到91 | ||
| -- | °C | 160 | ||
| 0.45MPa, unannealed | °C | 109到133 | ||
| 1.8MPa, unannealed | °C | 58到91 | ||
| 0.45MPa, unannealed | °C | 110到139 | ||
| -- | °C | 165到182 | ||
| mm/mm/°C | 83.8E-5到101.6E-5 | |||
| °C | 88到157 | |||
| °C | 85到156 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 23℃ | ohms·cm | 1.0E+13到1.0E+15 | ||
| Surface resistivity | ohms | 1.0E+14到1.0E+15 | ||
| Leakage Trace Index | V | 596到600 | ||
| 23℃ | ohms·cm | 9.8E+15到1.0E+16 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| gloss | 46到47 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot filament ignition temperature | °C | 548到804 | ||
| Burning wire flammability index | °C | 643到960 | ||
| Extreme Oxygen Index | % | 21 | ||
| Burning rate | mm/min | 0.0到101.6 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.