PA6/66 Ultramid® C3U BK BASF GERMANY

292

Unit Price:$10493 USD/MT

Packaging Specification:: 25 KG/PKG

Supply Quantity:: 10.5MT

Delivery Terms:: FOB

Port of Loading:: China Main Port

Accepted Payment Methods:: T/T

Shipping:: Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High impact resistance Flame retardant
Application Areas:Electronic insulation Electrical components
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
density		ASTMD792	1.16	g/cm³
density	density		ISO1183	1.16	g/cm³
Melt Volume-Flow Rate (MVR)	275°C/5.0kg	ISO1133	140	cm3/10min
Shrinkage rate	MD：3.18mm		0.80	%
Water absorption rate	Saturation	ASTMD570	8.5	%
	Water absorption rate	Saturation,23°C	ISO62	8.5	%
		Water absorption rate	Equilibrium,50%RH	ASTMD570	2.9	%
		Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	2.9	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	23°C	ISO527-2	3500	Mpa
tensile strength	Yield,23°C	ASTMD638	83.0	Mpa
Impact strength of cantilever beam gap	-40°C	ASTMD256	32	J/m
	Impact strength of cantilever beam gap	23°C	ASTMD256	43	J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO180	4.5	kJ/m²
Ball pressure hardness		ISO2039-1	100	Mpa
tensile strength	Yield,23°C	ISO527-2	75.0	Mpa
elongation	Yield,23°C	ASTMD638	5.0	%
	elongation	Yield,23°C	ISO527-2	4.0	%
	elongation	elongation	Break,23°C	ASTMD638	50	%
Nominal tensile fracture strain	23°C	ISO527-2	6.0	%
Bending modulus	23°C	ASTMD790	3000	Mpa
Bending modulus	Bending modulus	23°C	ISO178	3000	Mpa
Charpy Notched Impact Strength	-30°C	ISO179	4.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179	9.0	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO179	80	kJ/m²

Thermal performance	Test Condition	Test Method	Test Result	Unit
Linear coefficient of thermal expansion	MD		8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD		9E-05	cm/cm/°C
RTIElec	0.38mm	UL746	110	°C
	RTIElec	0.75mm	UL746	120	°C
		RTIElec	1.5mm	UL746	120	°C
		RTIElec	RTIElec	3.0mm	UL746	120	°C
RTI Imp	0.38mm	UL746	65.0	°C
	RTI Imp	0.75mm	UL746	105	°C
		RTI Imp	1.5mm	UL746	105	°C
		RTI Imp	RTI Imp	3.0mm	UL746	105	°C
Hot deformation temperature	0.45MPa,Unannealed	ASTMD648	224	°C
	Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	91.0	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	70.0	°C
Peak melting temperature		ASTMD3418	243	°C
Melting temperature		ISO3146	243	°C
Linear coefficient of thermal expansion	MD	ASTME831	4E-05	cm/cm/°C
RTIStr	0.38mm	UL746	65.0	°C
	RTIStr	0.75mm	UL746	115	°C
		RTIStr	1.5mm	UL746	120	°C
		RTIStr	RTIStr	3.0mm	UL746	120	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
VolumeResistivity	1.50mm	ASTMD257	1E+13	ohms·cm
Volume resistivity		IEC60093	1E+13	ohms·cm
Dielectric strength		IEC60243-1	32	KV/mm
Dielectric constant	1MHz	IEC60250	3.60
Dissipation factor	1MHz	IEC60250	0.020
Leakage Trace Index		IEC60112	600	V

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.38mm	UL94	V-0
	UL flame retardant rating	0.75mm	UL94	V-0
		UL flame retardant rating	1.5mm	UL94	V-0
		UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.