POM/PTFE Iupital™ FL2020 MITSUBISHI ENGINEERING JAPAN
245
Unit Price:$16636 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Weather resistance Medium viscosity
- Application Areas:Electronic and Electrical Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.00mm | 2.0 | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.19 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.18 | % | |
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 6.0 | g/10min |
| Melt Volume-Flow Rate (MVR) | 190°C/2.16kg | ISO1133 | 4.70 | cm3/10min |
| Shrinkage rate | MD：3.00mm | 2.1 | % | |
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 7.5 | g/10min |
| Melt Volume-Flow Rate (MVR) | 190°C/2.16kg | ISO1133 | 6.10 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 2400 | Mpa | |
| tensile strength | Yield | ISO527-2 | 44.0 | Mpa |
| Nominal tensile fracture strain | ISO527-2 | 15 | % | |
| Bending modulus | ISO178 | 2200 | Mpa | |
| bending strength | ISO178 | 67.0 | Mpa | |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 50 | kJ/m² |
| Tensile modulus | ISO527-2 | 2650 | Mpa | |
| tensile strength | Yield | ISO527-2 | 52.0 | Mpa |
| elongation | Yield | ISO527-2 | 8.0 | % |
| Nominal tensile fracture strain | ISO527-2 | 18 | % | |
| Bending modulus | ISO178 | 2400 | Mpa | |
| bending strength | ISO178 | 77.0 | Mpa | |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 60 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 0.45MPa, unannealed | ISO75-2/B | 154 | °C | |
| 1.8MPa, unannealed | ISO75-2/A | 97.0 | °C | |
| Melting temperature | ISO11357-3 | 166 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| TD | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 151 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 96.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+16 | ohms | |
| Volume resistivity | IEC60093 | 1E+14 | ohms·cm | |
| Dielectric strength | 1.00mm | IEC60243-1 | 25 | KV/mm |
| 3.00mm | IEC60243-1 | 16 | KV/mm | |
| Leakage Trace Index | IEC60112 | 600 | V |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| 0.800mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.