PC/PET XYLEX™ X7300CL-GY8C088T SABIC INNOVATIVE US
178
Unit Price:$4026 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 42MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:UV resistance｜High mobility
- Application Areas:Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 265°C/2.16kg | ASTMD1238 | 21 g/10min |
| Melt Volume flow Rate | 265°C/2.16kg | ISO1133 | 21.0 cm3/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.40to0.80 % |
| TD：3.20mm | 内部方法 | 0.50to0.70 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| TD：23to60°C | ISO11359-2 | 8.5E-05 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 102 °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 88.0 °C | |
| 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 90.0 °C | |
| Vicat Softening Temperature | ASTMD15259 | 108 °C | |
| ISO306/B120 | 106 °C | ||
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 1.2E-04 cm/cm/°C |
| MD：23到60°C | ISO11359-2 | 8.5E-05 cm/cm/°C |
| Optical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Transmittance | 2540µm | ASTMD1003 | 88.0 % |
| Haze | 2540µm | ASTMD1003 | 2.0 % |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | ASTMD638 | 1840 Mpa | |
| ISO527-2/1 | 1900 Mpa | ||
| Tensile Strength | 屈服 | ASTMD638 | 49.0 Mpa |
| Tensile Stress | 屈服 | ISO527-2/50 | 55.0 Mpa |
| Tensile Strength | 断裂 | ASTMD638 | 52.0 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 55.0 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 5.0 % |
| Tensile Strain | 屈服 | ISO527-2/50 | 5.0 % |
| Tensile Elongation | 断裂 | ASTMD638 | 150 % |
| Tensile Strain | 断裂 | ISO527-2/50 | >150 % |
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 1940 Mpa |
| ISO178 | 2000 Mpa | ||
| Flexural Strength | ISO178 | 71.0 Mpa | |
| 屈服,50.0mm跨距 | ASTMD790 | 83.0 Mpa |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Notched Izod Impact Strength | 23°C | ISO180/1A | 9.0 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 95.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.