EAA PRIMACOR™ 1410 STYRON US
307
Unit Price:$3478 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High toughness Heat sealing performance high strength
- Application Areas:film
- Color:--
- Grade:Blow molding grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 190℃/2.16kg | ASTM D-1238 | 1.5 | g/10min |
| 190℃/2.16kg | ISO 1133 | 1.5 | g/10min | |
| Monomer content | % | Internal Method | ||
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238,ISO1133 | 1.5 | g/10min |
| Content of comonomer | 内部方法 | 9.7 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | Yield,Compression Molded4 | ASTMD638 | 8.39 | Mpa |
| Yield,Compression Molded | ISO527-2/508 | 8.39 | Mpa | |
| Break,Compression Molded4 | ASTMD638 | 22.5 | Mpa | |
| Break,Compression Molded | ISO527-2/508 | 22.5 | Mpa | |
| elongation | Break,Compression Molded4 | ASTMD638 | 640 | % |
| Break,Compression Molded | ISO527-2/508 | 640 | % | |
| Tensile yield strength | Compression Molded | ASTM D-638 | Mpa | |
| Compression Molded | Mpa | |||
| Tensile fracture strength | Compression Molded | ASTM D-638 | Mpa | |
| Compression Molded | Mpa | |||
| Tensile strain at break | Compression Molded | ASTM D-638 | % | |
| Compression Molded | % | |||
| Tensile elongation at break (MD) | 50.8um | ASTM D-882 | 400 | % |
| 50.8um | ISO 527-3 | 400 | % | |
| Tensile elongation at break (TD) | 50.8um | ISO 527-3 | % | |
| Falling hammer impact | 50.8um | ASTM D-1709B | ||
| 50.8um | ||||
| Elmendorf Tear Strength (TD) | 50.8um | ASTM D-1922 | ||
| Elmendorf Tear Strength (MD) | 50.8um | ASTM D-1922 | ||
| 50.8um | ISO 6383-2 | 1700 | N | |
| Elmendorf Tear Strength (TD) | 50.8um | ISO 6383-2 | 2300 | N |
| Film thickness - Tested | um | 50.8 | ||
| Tensile yield strength (MD) | 50.8um | ASTM D-882 | Mpa | |
| Tensile yield strength (TD) | 50.8um | ASTM D-882 | Mpa | |
| 50.8um | ISO 527-3 | Mpa | ||
| Tensile yield strength (MD) | 50.8um | ISO 527-3 | Mpa | |
| Tensile fracture strength (TD) | 50.8um | ASTM D-882 | Mpa | |
| Tensile strength at break (MD) | 50.8um | ASTM D-882 | Mpa | |
| 50.8um | ISO 527-3 | Mpa | ||
| Tensile fracture strength (TD) | 50.8um | ISO 527-3 | Mpa | |
| Tensile elongation at break (TD) | 50.8um | ASTM D-882 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | ASTM D-1525 | ℃ | ||
| ISO 306 | ℃ | |||
| Melting temperature | ℃ | Internal Method | 97.8 | |
| vicat softening point | ASTMD1525,ISO306 | 81.1 | °C | |
| Melting temperature | 内部方法 | 97.8 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | MD:Yield,51μm | ASTMD882 | 11.8 | Mpa |
| TD:Yield,51μm | ASTMD882 | 10.9 | Mpa | |
| MD:Yield,51μm | ISO527-3 | 11.8 | Mpa | |
| TD:Yield,51μm | ISO527-3 | 10.9 | Mpa | |
| MD:Break,51μm | ASTMD882,ISO527-3 | 37.9 | Mpa | |
| TD:Break,51μm | ASTMD882,ISO527-3 | 38.1 | Mpa | |
| elongation | MD:Break,51μm | ASTMD882,ISO527-3 | 400 | % |
| TD:Break,51μm | ASTMD882,ISO527-3 | 470 | % | |
| Falling hammer impact | 51µm | ASTMD1709B,ISO7765-1/B | 580 | g |
| Elmondov tear strength | MD:51µm | ASTMD1922 | 380 | g |
| TD:51µm | ASTMD1922 | 510 | g | |
| MD:51µm | ISO6383-2 | 1700 | N | |
| TD:51µm | ISO6383-2 | 2300 | N |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| gloss | 45°，50.8um | ASTM D-2457 | ||
| Haze | 50.8um | ISO 14782 | % | |
| 50.8um | ASTM D-1003 | % | ||
| gloss | 45°,50.8µm | ASTMD2457 | 65 | |
| Haze | 50.8µm | ASTMD1003 | 5.8 | % |
| 50.8µm | ISO14782 | 5.8 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.