PC/PBT XENOY™ 6620U-BK1066 SABIC INNOVATIVE SHANGHAI
153
Unit Price:$2794 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 78MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Chemical resistance Low temperature impact re
- Application Areas:Plastic bag Lighting applications Household daily necessiti
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 1.6to1.8 | % |
| TD：3.20mm | 内部方法 | 1.6to1.8 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.14 | % |
| Specific volume | ASTMD792 | 0.835 | cm³/g | |
| Melt mass flow rate | 266°C/5.0kg | ASTMD1238 | 22 | g/10min |
| Melt Volume-Flow Rate (MVR) | 265°C/5.0kg | ISO1133 | 17.1 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Suspended wall beam gap impact strength | -30°C | ISO180/1A | 51 | kJ/m² |
| 23°C | ISO180/1A | 54 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 56.3 | J |
| Tensile modulus | ASTMD638 | 1780 | Mpa | |
| ISO527-2/1 | 1830 | Mpa | ||
| tensile strength | Yield | ASTMD638 | 43.7 | Mpa |
| Yield | ISO527-2/50 | 41.1 | Mpa | |
| Break | ASTMD638 | 32.9 | Mpa | |
| Break | ISO527-2/50 | 31.7 | Mpa | |
| elongation | Yield | ASTMD638 | 4.2 | % |
| Yield | ISO527-2/50 | 3.9 | % | |
| Break | ASTMD638 | 150 | % | |
| Break | ISO527-2/50 | 19 | % | |
| Bending modulus | 50.0mmSpan | ASTMD790 | 1780 | Mpa |
| ISO178 | 1700 | Mpa | ||
| Bending strength 5, | ISO178 | 60.0 | Mpa | |
| bending strength | Yield,50.0mmSpan | ASTMD790 | 63.6 | Mpa |
| Impact strength of simply supported beam gap | 23°C | ISO179/1eA | 72 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 98.9 | °C |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 60.0 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 50.5 | °C | |
| vicat softening point | ASTMD152510 | 123 | °C | |
| -- | ISO306/B50 | 119 | °C | |
| -- | ISO306/B120 | 122 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 9.9E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 9.9E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 1E-04 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| RTIElec | UL746 | 75.0 | °C | |
| RTI Imp | UL746 | 75.0 | °C | |
| RTIStr | UL746 | 75.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Arc resistance | ASTMD495 | PLC5 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC0 | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC1 | |
| Hot wire ignition | HWI | UL746 | PLC3 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.