PC/PBT CYCOLOY™ 1731J-1001 SABIC INNOVATIVE JAPAN
247
Unit Price:$2835 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 78MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Chemical resistance High impact resistance High mobility UV resistance
- Application Areas:medical care Plastic bag Gears Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Specific volume | ASTMD792 | 0.820 | cm³/g | |
| Melt mass flow rate | 250°C/5.0kg | ASTMD1238 | 9.6 | g/10min |
| 250°C/5.0kg | ISO1133 | 8.0 | g/10min | |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| TD：3.20mm | 内部方法 | 0.60to0.80 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.28 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.080 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ASTMD638 | 2370 | Mpa | |
| ISO527-2/1 | 2330 | Mpa | ||
| tensile strength | Yield | ASTMD638 | 61.4 | Mpa |
| Yield | ISO527-2/50 | 60.0 | Mpa | |
| Break | ASTMD638 | 56.0 | Mpa | |
| Break | ISO527-2/50 | 58.0 | Mpa | |
| elongation | Yield | ASTMD638 | 5.0 | % |
| Yield | ISO527-2/50 | 5.0 | % | |
| Break | ASTMD638 | 100 | % | |
| Break | ISO527-2/50 | 90 | % | |
| Bending modulus | 50.0mmSpan | ASTMD790 | 2340 | Mpa |
| ISO178 | 2210 | Mpa | ||
| Bending strength 5, | ISO178 | 93.0 | Mpa | |
| bending strength | Yield,50.0mmSpan | ASTMD790 | 93.1 | Mpa |
| Impact strength of simply supported beam gap | 23°C | ISO179/1eA | 65 | kJ/m² |
| Suspended wall beam gap impact strength | -30°C | ISO180/1A | 16 | kJ/m² |
| 23°C | ISO180/1A | 59 | kJ/m² | |
| Dart impact equipped with measuring instruments | -30°C,TotalEnergy | ASTMD3763 | 61.5 | J |
| 23°C,TotalEnergy | ASTMD3763 | 61.1 | J |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 116 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 93.0 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 107 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 99.0 | °C | |
| vicat softening point | ASTMD152510 | 125 | °C | |
| -- | ISO306/B50 | 127 | °C | |
| -- | ISO306/B120 | 130 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7.8E-05 | cm/cm/°C |
| MD：-40to95°C | ASTME831 | 8.3E-05 | cm/cm/°C | |
| MD：-40to40°C | ISO11359-2 | 7.8E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7.6E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 7.6E-05 | cm/cm/°C | |
| RTIElec | UL746 | 75.0 | °C | |
| RTI Imp | UL746 | 75.0 | °C | |
| RTIStr | UL746 | 75.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Arc resistance | ASTMD495 | PLC5 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC2 | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC2 | |
| Hot wire ignition | HWI | UL746 | PLC2 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.