PCTG Tritan™ 6002 EASTMAN USA
277
Unit Price:$3012 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 171.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Chemical resistance Hydrolysis resistance
- Application Areas:Electrical applications Household daily necessiti
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 300°C/1.2 kg | ASTM D1238 | 20 | g/10 min |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.30 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.15 | % | |
| density | D792 | 1.2 | ||
| General transmittance | D1003 | 89% | ||
| Total transmittance | D1003 | 91% | ||
| Light Mist | D1003 | 0.3% |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | @Yield | D638 | 47MPa（6900 psi） | |
| @Break | D638 | 51MPa（7400 psi） | ||
| tensile strength | @Yield | ISO 527 | 47MPa | |
| @Break | ISO 527 | 46MPa | ||
| Rockwell hardness | R刻度 | D785 | 103 | |
| Stretching degree | @Yield | D638 | 5% | |
| @Break | D638 | 320% | ||
| Flexural modulus | D790 | 2000MPa(2.9×10 | ||
| ISO 178 | 1850MPa | |||
| Flexural strength | ISO 178 | 65MPa | ||
| Tensile modulus | ISO 527 | 1800MPa | ||
| Impact resistance (perforation), energy @ maximum load | @23℃(73℉) | D3763 | 42 J(31 ft bf) | |
| @-40℃(-40℉) | D3763 | 48 J/m(35 ft bf) | ||
| Suspended beam impact strength | @23℃，切口 | ISO 180 | 7.8kJ/m | |
| @-40℃，切口 | ISO 180 | 4.8kJ/m | ||
| tensile strength | Yield | ASTM D638 | 60.0 | Mpa |
| elongation | Break | ASTM D638 | 15 | % |
| impact strength | @23℃(73℉)，未切口 | D4812 | NB J/m(NB ft bf/in) | |
| @-40℃(-40℉)，未切口 | D4812 | NB J/m(NB ft bf/in) | ||
| Suspended beam impact strength | @23℃(73?H)，切口 | D256 | 80 J/m(1.5 ft bf/in) | |
| @-40℃(-40?H)，切口 | D256 | 40 J/m(0.7 ft bf/in) | ||
| Stretching degree | @Yield | ISO 527 | 4% | |
| @Break | ISO 527 | 200% | ||
| Flexural yield strength | D790 | 69MPa(10000 psi) |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending temperature | 0.455MPa(66 psi) | D648 | 73℃(164℉) | |
| 1.82MPa(264 psi) | D648 | 65℃(149℉) | ||
| Hot deformation temperature | 0.45 MPa, Unannealed | ASTM D648 | 135 | °C |
| 1.8 MPa, Unannealed | ASTM D648 | 125 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTM D257 | > 1.0E+16 | ohms·cm | |
| Dielectric strength | 2.00 mm | ASTM D149 | 15 | KV/mm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 120 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Temperature at the rear of the barrel | 265 到 275 | °C | ||
| Temperature in the middle of the barrel | 280 到 290 | °C | ||
| Spray nozzle temperature | 285 到 295 | °C | ||
| Processing (melt) temperature | 280 到 290 | °C | ||
| Mold temperature | 60 到 80 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 3.2 mm | UL 94 | V-2 |
| Processing conditions | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Plastic film temperature | 15-30℃(60-80℉) | |||
| drying temperature | 70℃(160℉) | |||
| Processing melting temperature | 230-280℃(450-530℉) | |||
| drying time | 6小时 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.