Physical	Test Condition	Test Method	Test Result
Melt Mass-Flow Rate	220°C/10.0 kg	ASTM D1238	8.8 g/10 min
	Melt Mass-Flow Rate	260°C/5.0 kg	ASTM D1238	7.1 g/10 min
	Melt Mass-Flow Rate	Melt Mass-Flow Rate	280°C/3.8 kg	ASTM D1238	7.2 g/10 min
Melt Volume flow Rate	260°C/5.0 kg	ISO 1133	9.00 cm3/10min
Modeling Shrinkage	流动 2	内部方法	0.40 到 0.70 %
	Modeling Shrinkage	流动 : 3.20 mm	内部方法	0.40 到 0.70 %
	Modeling Shrinkage	Modeling Shrinkage	横向流动 : 3.20 mm	内部方法	0.40 到 0.75 %
Moisture Absorption	饱和, 23°C	ISO 62	0.50 %
Moisture Absorption	Moisture Absorption	平衡, 23°C, 50% RH	ISO 62	0.20 %
Outdoor Suitability		UL 746C	f1

Thermal Properties	Test Condition	Test Method	Test Result
Deflection Temperature Under Load?	0.45 MPa, 未退火, 3.20 mm	ASTM D648	97.0 °C
	Deflection Temperature Under Load?	0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 11	ISO 75-2/Bf	98.0 °C
		Deflection Temperature Under Load?	1.8 MPa, 未退火, 3.20 mm	ASTM D648	84.0 °C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 11	ISO 75-2/Af	84.0 °C
Vicat Softening Temperature	--		98.0 °C
	Vicat Softening Temperature	--	ISO 306/B50	95.0 °C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	99.0 °C
Ball PressureTest	83 到 87°C	IEC 60695-10-2	通过
Linear thermal expansion coefficient	流动 : -40 到 40°C	ASTM E831	8.4E-5 cm/cm/°C
	Linear thermal expansion coefficient	流动 : -40 到 40°C	ISO 11359-2	8.3E-5 cm/cm/°C
		Linear thermal expansion coefficient	横向 : -40 到 40°C	ASTM E831	9.4E-5 cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	横向 : -40°C	ISO 11359-2	9.4E-5 cm/cm/°C

Optical	Test Condition	Test Method	Test Result
Gardner	60°, 无织构	ASTM D523	93

Flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	HB

Mechanical Properties	Test Condition	Test Method	Test Result
Tensile Modulus	-- 3	ASTM D638	2360 Mpa
	Tensile Modulus	-- 4	ASTM D638	2400 Mpa
	Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2350 Mpa
Tensile Strength	屈服 5	ASTM D638	46.0 Mpa
	Tensile Strength	屈服 6	ASTM D638	43.0 Mpa
		Tensile Strength	屈服	ISO 527-2/50	45.0 Mpa
			Tensile Strength	断裂 6	ASTM D638	36.0 Mpa
				Tensile Strength	断裂 5	ASTM D638	37.0 Mpa
				Tensile Strength	Tensile Strength	断裂	ISO 527-2/50	36.0 Mpa
Tensile Elongation	屈服 6	ASTM D638	2.5 %
	Tensile Elongation	屈服 5	ASTM D638	2.7 %
		Tensile Elongation	屈服	ISO 527-2/50	2.8 %
			Tensile Elongation	断裂 6	ASTM D638	27 %
				Tensile Elongation	断裂 5	ASTM D638	26 %
				Tensile Elongation	Tensile Elongation	断裂	ISO 527-2/50	36 %
Flexural Modulus	50.0 mm 跨距 7	ASTM D790	2450 Mpa
Flexural Modulus	Flexural Modulus	-- 8	ISO 178	2380 Mpa
Flexural Stress	-- 8, 9	ISO 178	64.0 Mpa
Flexural Stress	Flexural Stress	屈服, 50.0 mm 跨距 7	ASTM D790	74.0 Mpa

Injection	Test Condition	Test Method	Test Result
Drying Temperature			85 到 90 °C
Drying Time			4.0 hr
Suggested Max Moisture			0.040 %
Suggested Shot Size			40 到 80 %
Rear Temperature			215 到 250 °C
Middle Temperature			220 到 255 °C
Front Temperature			230 到 260 °C
Nozzle Temperature			220 到 255 °C
Processing (Melt) Temp			240 到 270 °C
Mold Temperature			60 到 85 °C
Back Pressure			0.300 到 1.00 Mpa
Screw Speed			30 到 80 rpm
Vent Depth			0.038 到 0.076 mm

Hardness	Test Condition	Test Method	Test Result
Rockwell Hardness	R 级	ASTM D785	100

Impact Properties	Test Condition	Test Method	Test Result
Instrumented Dart Impact	-30°C, Total Energy	ASTM D3763	3.00 J
Instrumented Dart Impact	Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	36.0 J

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.