MVLDPE DOWLEX™ 2045G STYRON US
259
Unit Price:$1463 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high strength
- Application Areas:film
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D-792 | 0.92 | g/m3 | |
| Melt flow rate | 190℃/2.16kg | ASTM D-1238 | 1 | g/10min |
| film thickness | 50.8 | um | ||
| Melt mass flow rate | ℃/Kg | ASTMD1238 | 1.0 | g/10min |
| 厚度 | 50.8 | microns |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | ASTMD882 | 10.89 | Mpa | |
| ASTMD882 | 12.29 | Mpa | ||
| Secant modulus | ASTMD882 | 194.4 | Mpa | |
| ASTMD882 | 232.6 | Mpa | ||
| tensile strength | ASTMD882 | 55.11 | Mpa | |
| ASTMD882 | 49.81 | Mpa | ||
| impact force | 235 | ft-lbf/in3 | ||
| elongation | Break | ASTMD882 | 827 | % |
| Break | ASTMD882 | 889 | % | |
| Elmendorf tear strength | ASTMD192 | 902 | g | |
| ASTMD192 | 1200 | g | ||
| Falling hammer impact | ASTMD1709 | 288 | g | |
| Tangent modulus (MD) | 2% Secant，50.8um | ASTM D-882 | 194 | Mpa |
| Tangent modulus (TD) | 2% Secant，50.8um | ASTM D-882 | 233 | Mpa |
| Tensile yield strength (MD) | 50.8um | ASTM D-882 | 10.9 | Mpa |
| Tensile yield strength (TD) | 50.8um | ASTM D-882 | 12.3 | Mpa |
| Tensile fracture strength (TD) | 50.8um | ASTM D-882 | 55.1 | Mpa |
| Tensile strength at break (MD) | 50.8um | ASTM D-882 | 49.8 | Mpa |
| Tensile elongation at break (TD) | 50.8um | ASTM D-882 | 890 | % |
| Tensile elongation at break (MD) | 50.8um | ASTM D-882 | 830 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | ASTM D-1525 | 108 | °C | |
| Melting temperature | Internal Method | 122 | °C | |
| vicat softening point | ASTM1525 | 108 | °C | |
| Melting Temperature | 陶氏化学方法(DSC | 122 | °C |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Movie Piercing Resistance | 50.8um | Internal Method | 19.4 | J/cm³ |
| Film Resilience (MD) | 50.8um | ASTM D-882 | 346 | J/cm³ |
| Film Resilience (TD) | 50.8um | ASTM D-882 | 351 | J/cm4 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| gloss | 45°，50.8um | ASTM D-2457 | 60 | |
| Haze | 50.8um | ASTM D-1003 | 10 | % |
| gloss | ASTM2457 | 60 | ||
| Haze | ASTMD1003 | 10 | % |
| Processing conditions | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Temperature | 232 | °C |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Elmendorf tear strength | ASTMD1922 | 17.8 | g/micron | |
| ASTMD1922 | 23.6 | g/micron | ||
| impact force | ASTMD882 | 4176 | ft-lbf/in3 | |
| ASTMD882 | 4241 | ft-lbf/in3 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.