COC TOPAS® 8007F-600 JAPAN POLYPLASTIC
151
Unit Price:$11488 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 35.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Dimensional stability Chemical resistance
- Application Areas:LCD application Optical applications
- Color:--
- Grade:Food grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 1.8 | g/10min |
| 230°C/2.16kg | ISO1133 | 10 | g/10min | |
| Melt Volume-Flow Rate (MVR) | 190°C/2.16kg | ISO1133 | 2.00 | cm3/10min |
| 230°C/2.16kg | ISO1133 | 11.0 | cm3/10min | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.010 | % |
| (23°C,24hr) | ISO62 | 0.01 | % | |
| Melt mass flow rate | 260℃/2.16Kg | ISO1133 | 32 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 23°C | ISO527-2 | 63 | Mpa |
| elongation at break | 23°C | ISO527-2 | 4.5 | % |
| Tensile modulus | 23°C | ISO527-2 | 2600 | Mpa |
| Impact strength of simply supported beam gap | 23°C | ISO179/1eA | 2.6 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 20 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPaUnannealed | ISO75-2/Bf | 75 | °C |
| vicat softening point | ISO306/B50 | 80 | °C | |
| 玻璃转化温度 | ISO11357-2 | 78 | °C | |
| Glass transition temperature | ISO11357-2 | 78.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistance | IEC60093 | 1E+14 | Ω.cm | |
| Dielectric constant | 23°C | IEC60250 | 2.35 | 1kHz |
| Dissipation factor | 相对漏电起痕指数 | IEC60112 | 600 | V |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Film thickness - tested | 70 | µm | ||
| Tensile modulus | MD:70µm,铸造薄膜 | ISO527-3/1 | 2100 | Mpa |
| TD:70µm,铸造薄膜 | ISO527-3/1 | 1700 | Mpa | |
| Tensile stress | MD:Break,70μm,铸造薄膜 | ISO527-3/50 | 55.0 | Mpa |
| TD:Break,70μm,铸造薄膜 | ISO527-3/50 | 50.0 | Mpa | |
| elongation | MD:Break,70μm,铸造薄膜 | ISO527-3/50 | 3.4 | % |
| TD:Break,70μm,铸造薄膜 | ISO527-3/50 | 3.4 | % | |
| Water vapor permeability | 70µm,23°C,CastFilm,85%RH | ASTMF1249 | 0.10 | g·mm/m²/atm/24hr |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ISO489 | 1.53 | °C | |
| Transmittance 2000 μ m | ISO13468-2 | 91 | % | |
| gloss | 60°,70.0µm,铸造薄膜 | ISO2813 | >100 | |
| Haze | 70.0µm,铸造薄膜 | ISO14782 | >2.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.