COC TOPAS® 8007F-04 JAPAN POLYPLASTIC
213
Unit Price:$11902 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Dimensional stability Chemical resistance
- Application Areas:LCD application Optical applications
- Color:--
- Grade:Optical grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO62 | 0.01 | % |
| Melt mass flow rate | 190℃/2.16Kg | ISO1133 | 1.8 | g/10min |
| 230℃/2.16Kg | ISO1133 | 11 | g/10min | |
| 水蒸气渗透性 | 3.70 | gmil/(m2day | ||
| 氧渗透 | 997 | cm3mil/(m2dayatm | ||
| 水蒸气穿透率 | ISO15106-3 | 0.0008 | g/m²/day | |
| 厚度 | 70 | microns | ||
| 260℃/2.16Kg | ISO1133 | 32 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 23°C | ISO527-2 | 63 | Mpa |
| elongation at break | 23°C | ISO527-2 | 4.5 | % |
| Tensile modulus | 23°C | ISO527-2 | 2600 | Mpa |
| Impact strength of simply supported beam gap | 23°C | ISO179/1eA | 2.6 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 20 | kJ/m² |
| elongation at break | MD,23°C | ISO527-2 | 2.9 | % |
| TD,23°C | ISO527-2 | 3 | % | |
| Tensile modulus | TD,23°C | ISO527-2 | 1800 | Mpa |
| MD,23°C | ISO527-2 | 2200 | Mpa | |
| Break拉伸强度 | ISO527-3 | 57 | Mpa | |
| Break拉伸强度 | ISO527-3 | 50 | Mpa | |
| Elmendorf撕裂强度 | ISO6383-2 | 225 | g | |
| Elmendorf撕裂强度 | ISO6383-2 | 230 | g | |
| 跌落试验 | ISO7765-1 | <=36 | g |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPaUnannealed | ISO75-2/Bf | 75 | °C |
| vicat softening point | ISO306/B50 | 80 | °C | |
| 玻璃转化温度 | ISO11357-2 | 78 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistance | IEC60093 | 1E+14 | Ω.cm | |
| Dielectric constant | 23°C | IEC60250 | 2.35 | 1kHz |
| Dissipation factor | 相对漏电起痕指数 | IEC60112 | 600 | V |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ISO489 | 1.53 | °C | |
| Transmittance 2000 μ m | ISO13468-2 | 91 | % | |
| Haze | ISO13468-2 | <=0.1 | % | |
| gloss | ISO2813 | >=100 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.