PA610 LNP™ LUBRICOMP™ QFL-4036 SABIC INNOVATIVE US
273
Unit Price:$5456 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Conductive Glass fiber reinforced
- Application Areas:Electronic and Electrical Fitness equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD:24hr | ASTMD955 | 0.70 | % |
| TD:24hr | ISO294-4 | 0.70 | % | |
| MD:24hr | ISO294-4 | 0.17 | % | |
| Water absorption rate | 24hr,50%RH | ASTMD570 | 0.14 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.22 | % | |
| Shrinkage rate | MD:24hr | ASTMD955 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | --3 | ASTMD638 | 11000 | Mpa |
| -- | ISO527-2/1 | 9800 | Mpa | |
| tensile strength | Break | ASTMD638 | 149 | Mpa |
| Break | ISO527-2 | 150 | Mpa | |
| elongation | Break | ASTMD638,ISO527-2 | 2.6 | % |
| Bending modulus | -- | ASTMD790 | 8480 | Mpa |
| -- | ISO178 | 9700 | Mpa | |
| bending strength | -- | ASTMD790 | 221 | Mpa |
| -- | ISO178 | 228 | Mpa | |
| friction coefficient | Dynamic | ASTMD3702Modified | 0.71 | |
| Static | ASTMD3702Modified | 0.52 | ||
| Wear factor - Washer | ASTMD3702Modified | 15.0 | 10^-10in^5-min/ft-lb-hr | |
| Cantilever beam without notch impact strength | 23°C | ASTMD4812 | 940 | J/m |
| 23°C4 | ISO180/1U | 65 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 8.50 | J |
| -- | ISO6603-2 | 3.19 | J |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 224 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 216 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan5 | ISO75-2/Af | 211 | °C | |
| Linear coefficient of thermal expansion | MD:-40to40°C | ASTME831,ISO11359-2 | 2.9E-05 | cm/cm/°C |
| TD:-40to40°C | ASTME831 | 7.4E-05 | cm/cm/°C | |
| TD:-40to40°C | ISO11359-2 | 7.5E-05 | cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.