PEI ULTEM™ 1010-7A1D128 SABIC INNOVATIVE US
133
Unit Price:$21796 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan transparent enhance Flame retardant
- Application Areas:Food service sector
- Color:--
- Grade:High liquidity level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 337°C/6.6 kg | ASTM D1238 | 18 | g/10 min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Water absorption rate | 24 hr | ASTM D570 | 0.25 | % |
| Equilibrium, 23°C | ASTM D570 | 1.3 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ASTM D785 | 109 | |
| Tensile modulus | ASTM D638 | 3580 | Mpa | |
| tensile strength | Yield | ASTM D638 | 110 | Mpa |
| Elongation rate | Yield | ASTM D638 | 7.0 | % |
| Break | ASTM D638 | 60 | % | |
| Bending modulus | 100 mm Span | ASTM D790 | 3510 | Mpa |
| bending strength | Yield, 100 mm Span | ASTM D790 | 165 | Mpa |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 Wheel | ASTM D1044 | 10.0 | mg |
| Non notched cantilever beam impact | 23°C | ASTM D4812 | 1300 | J/m |
| Reverse notch impact | 3.20 mm | ASTM D256 | 1200 | J/m |
| Falling hammer impact | 23°C | ASTM D3029 | 33.0 | J |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 207 | °C |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 198 | °C | |
| vicat softening point | ASTM D15255 | 218 | °C | |
| Linear coefficient of thermal expansion - flow | -20 to 150°C | ASTM E831 | 5.6E-5 | cm/cm/°C |
| thermal conductivity | ASTM C177 | 0.22 | W/m/K | |
| RTI Elec | UL 746 | 170 | °C | |
| RTI Imp | UL 746 | 170 | °C | |
| RTI | UL 746 | 170 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.0E+17 | ohms·cm | |
| Dielectric strength | 1.60 mm, in Air | ASTM D149 | 33 | KV/mm |
| 1.60 mm, in Oil | ASTM D149 | 28 | KV/mm | |
| Dielectric constant | 1 kHz | ASTM D150 | 3.15 | |
| Dissipation factor | 1 kHz | ASTM D150 | 1.3E-3 | |
| 2.45 GHz | ASTM D150 | 2.5E-3 | ||
| Arc resistance | ASTM D495 | PLC 5 | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 4 | ||
| High arc combustion index (HAI) | UL 746 | PLC 3 | ||
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 2 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 1 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 150 | °C | ||
| drying time | 4.0 到 6.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 40 到 60 | % | ||
| Temperature at the rear of the barrel | 330 到 400 | °C | ||
| Temperature in the middle of the barrel | 340 到 400 | °C | ||
| Temperature at the front of the material cylinder | 345 到 400 | °C | ||
| Spray nozzle temperature | 345 到 400 | °C | ||
| Processing (melt) temperature | 350 到 400 | °C | ||
| Mold temperature | 135 到 165 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 40 到 70 | rpm | ||
| Exhaust hole depth | 0.025 到 0.076 | mm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94 | V-0 | |
| 3.0 mm | UL 94 | 5VA | ||
| Extreme Oxygen Index | ASTM D2863 | 44 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.