PEI ULTEM™ AUT200 BK1A113 SABIC INNOVATIVE SPAIN
162
Unit Price:$11107 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 100MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility High transparency high definition
- Application Areas:Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 337°C/6.6kg | ASTMD1238 | 18 | g/10min |
| Melt Volume-Flow Rate (MVR) | 360°C/5.0kg | ISO1133 | 25.0 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 1.3 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus | 50.0mmSpan | ASTMD790 | 3520 | Mpa |
| Tensile modulus | ASTMD638 | 3590 | Mpa | |
| ISO527-2/1 | 3200 | Mpa | ||
| tensile strength | Yield | ASTMD638 | 110 | Mpa |
| Yield | ISO527-2/5 | 105 | Mpa | |
| Break | ASTMD638 | 105 | Mpa | |
| Break | ISO527-2/5 | 85.0 | Mpa | |
| elongation | Yield | ASTMD638 | 7.0 | % |
| Yield | ISO527-2/5 | 6.0 | % | |
| Break | ASTMD638 | 60 | % | |
| Break | ISO527-2/5 | 60 | % | |
| Bending modulus | ISO178 | 3300 | Mpa | |
| Bending strength 5, | ISO178 | 160 | Mpa | |
| bending strength | Yield,50.0mmSpan | ASTMD790 | 165 | Mpa |
| Impact strength of simply supported beam gap | 23°C | ISO179/1eA | 3.0 | kJ/m² |
| Suspended wall beam gap impact strength | -30°C | ISO180/1A | 5.0 | kJ/m² |
| 23°C | ISO180/1A | 5.0 | kJ/m² | |
| Unscented Izod Impact Strength | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 33.0 | J |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 205 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 197 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 199 | °C | |
| 1.8MPa,Unannealed,100mmSpan9 | ISO75-2/Ae | 190 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan10 | ISO75-2/Af | 193 | °C | |
| vicat softening point | ASTMD152511 | 219 | °C | |
| -- | ISO306/B50 | 211 | °C | |
| -- | ISO306/B120 | 212 | °C | |
| Linear coefficient of thermal expansion | MD：-40to150°C | ASTME831 | 5.5E-05 | cm/cm/°C |
| MD：23to150°C | ISO11359-2 | 5E-05 | cm/cm/°C | |
| TD：-40to150°C | ASTME831 | 5.5E-05 | cm/cm/°C | |
| TD：23to150°C | ISO11359-2 | 5E-05 | cm/cm/°C |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| MetallizedHazeOnset | 内部方法 | 204 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.