PEEK AVASPIRE® AV-750 SOLVAY USA
172
Unit Price:$88510 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 19MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 380°C/2.16 kg | ASTM D1238 | 7.0 | g/10 min |
| Shrinkage rate | Flow : 3.18 mm | ASTM D955 | 0.10 到 0.30 | % |
| Across Flow : 3.18 mm | ASTM D955 | 1.2 到 1.4 | % | |
| Water absorption rate | 24 hr | ASTM D570 | 0.10 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ASTM D785 | 105 | |
| Tensile modulus | -- 5 | ASTM D638 | 15100 | Mpa |
| -- | ISO 527-2/1A/1 | 16700 | Mpa | |
| tensile strength | Yield, 5.00 mm | ISO 527-2/1A/5 | 188 | Mpa |
| -- 6 | ASTM D638 | 191 | Mpa | |
| elongation | Break 5 | ASTM D638 | 1.8 | % |
| Break | ISO 527-2/1A/5 | 1.8 | % | |
| Bending modulus | -- | ASTM D790 | 14800 | Mpa |
| -- | ISO 178 | 15400 | Mpa | |
| bending strength | 23°C | ASTM D790 | 253 | Mpa |
| 250°C | ASTM D790 | 54.0 | Mpa | |
| -- | ISO 178 | 250 | Mpa | |
| compressive strength | ASTM D695 | 182 | Mpa | |
| shear strength | ASTM D732 | 89.0 | Mpa | |
| Non notched cantilever beam impact | -- | ASTM D4812 | 590 | J/m |
| -- | ISO 180 | 41 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, Annealed | ASTM D648 | 285 | °C |
| Glass transition temperature | ASTM D3418 | 150 | °C | |
| Peak melting temperature | ASTM D3418 | 345 | °C | |
| Linear coefficient of thermal expansion - flow | -50 to 50°C | ASTM E831 | 1.5E-5 | cm/cm/°C |
| specific heat | 50°C | DSC | 1260 | J/kg/°C |
| 200°C | DSC | 1620 | J/kg/°C | |
| thermal conductivity | ASTM E1530 | 0.31 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTM D257 | > 1.9E+17 | ohms | |
| Volume resistivity | ASTM D257 | 1.8E+17 | ohms·cm | |
| Dielectric strength | ASTM D149 | 19 | KV/mm | |
| Dielectric constant | 60 Hz | ASTM D150 | 3.68 | |
| 1 kHz | ASTM D150 | 3.69 | ||
| 1 MHz | ASTM D150 | 3.66 | ||
| Dissipation factor | 60 Hz | ASTM D150 | 2.0E-3 | |
| 1 kHz | ASTM D150 | 1.0E-3 | ||
| 1 MHz | ASTM D150 | 3.0E-3 |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 400°C, 1000 sec^-1 | ASTM D3835 | 450 | Pa·s |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 150 到 175 | °C | ||
| drying time | 2.5 到 4.0 | hr | ||
| Processing (melt) temperature | 370 到 395 | °C | ||
| Mold temperature | 175 到 210 | °C | ||
| Back pressure | 0.138 到 0.345 | Mpa | ||
| Screw speed | 75 | rpm | ||
| Screw compression ratio | 2.0:1.0 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8 mm | UL 94 | V-1 | |
| 1.6 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.