TPE Hytrel® 8238 DuPont, European Union
153
Unit Price:$8896 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 21MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan
- Application Areas:Wire and cable Hose Joint Cable sheath Engine parts
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO1183 | 1.28 | g/cm³ | |
| Melt mass flow rate | 240°C/2.16kg | ISO1133 | 13 | g/10min |
| Melt Volume-Flow Rate (MVR) | 240°C/2.16kg | ISO1133 | 11.5 | cm3/10min |
| Shrinkage rate | TD | ISO294-4 | 1.6 | % |
| MD | ISO294-4 | 1.6 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.30 | % |
| Saturation,23°C,2.00mm | ISO62 | 0.60 | % | |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
| MediumDensity | 1.13 | g/cm³ | ||
| SpecificHeatCapacity of Melt | 2150 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.15 | W/m/K |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 1200 | Mpa | |
| Charpy Notched Impact Strength | -40°C | ISO179/1eA | 5.0 | kJ/m² |
| -30°C | ISO179/1eA | 5.0 | kJ/m² | |
| 23°C | ISO179/1eA | 15 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 5.5 | kJ/m² |
| 23°C | ISO180/1A | 11 | kJ/m² | |
| Tensile impact strength | 23°C | ISO8256/1 | 57.0 | kJ/m² |
| Shore hardness | Shore D | ISO868 | 76 | |
| Shore D,15sec | ISO868 | 70 | ||
| tensile strength | Yield | ISO527-2 | 38.0 | Mpa |
| Break | ISO527-2 | 46.0 | Mpa | |
| 10%Strain | ISO527-2 | 34.0 | Mpa | |
| 50%Strain | ISO527-2 | 28.0 | Mpa | |
| 100%Strain | ISO527-2 | 26.0 | Mpa | |
| elongation | Yield | ISO527-2 | 19 | % |
| Break | ISO527-2 | >300 | % | |
| Nominal tensile fracture strain | ISO527-2 | 340 | % | |
| Bending modulus | ISO178 | 1150 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40to23°C | ISO11359-2 | 1E-04 | cm/cm/°C |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 5.44E-08 | m²/s | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 105 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 45.0 | °C | |
| Brittle temperature | ISO974 | -84.0 | °C | |
| Glass transition temperature | ISO11357-2 | 50.0 | °C | |
| vicat softening point | -- | ISO306/A50 | 213 | °C |
| -- | ISO306/B50 | 150 | °C | |
| Melting temperature | ISO11357-3 | 221 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 1.5E-04 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 1.4E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 21 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 4.00 | |
| 1MHz | IEC60250 | 3.70 | ||
| Dissipation factor | 100Hz | IEC60250 | 0.010 | |
| 1MHz | IEC60250 | 0.018 | ||
| Leakage Trace Index | IEC60112 | 600 | V |
| elastomer | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tear strength | Across Flow | ISO34-1 | 210 | kN/m |
| 流量 | ISO34-1 | 230 | kN/m |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.9mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.9mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 22 | % | |
| FMVSS flammability | FMVSS302 | SE |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 550 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.