PA12 Pebax® 7033 SP 01 ARKEMA USA
160
Unit Price:$14473 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 59MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Low temperature resistanc
- Application Areas:Medical Supplies
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow | ISO 294-4 | 1.5 | % |
| 流量 | ISO 294-4 | 1.2 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 1.1 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Supporting hardness | Shore D, 15 sec | ISO 7619-1 | 61 | |
| Tensile modulus | ISO 527-2 | 414 | Mpa | |
| tensile strength | Yield | ISO 527-2 | 23.0 | Mpa |
| Break | ISO 527-2 | 54.0 | Mpa | |
| 10% Strain | ISO 527-2 | 22.0 | Mpa | |
| 100% Strain | ISO 527-2 | 21.0 | Mpa | |
| elongation | Yield | ISO 527-2 | 22 | % |
| Break | ISO 527-2 | > 300 | % | |
| Nominal tensile fracture strain | ISO 527-2 | > 50 | % | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 99.0 | °C |
| vicat softening point | ISO 306/B50 | 164 | °C | |
| Melting temperature | ISO 11357-3 | 172 | °C | |
| Linear coefficient of thermal expansion - flow | ISO 11359-2 | 1.6E-4 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | -- | ohms | |
| Leakage Trace Index | IEC 60112 | -- | V |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt density | 0.830 | g/cm³ | ||
| Thermal conductivity of melt | 0.20 | W/m/K | ||
| Specific Heat Capacity of Melt | 2700 | J/kg/°C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 70 到 80 | °C | ||
| drying time | 5.0 到 7.0 | hr | ||
| Processing (melt) temperature | 230 到 290 | °C | ||
| Mold temperature | 25 到 60 | °C |
| squeeze | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 70 到 80 | °C | ||
| drying time | 5.0 到 7.0 | hr | ||
| Melt Temperature | 220 到 250 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flammability level | 1.6 mm | IEC 60695-11-10, -20 | HB | |
| 3.1 mm | IEC 60695-11-10, -20 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.