PBT VALOX™ ENH4550-1001 SABIC INNOVATIVE SHANGHAI
137
Unit Price:$4467 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 33MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity high strength
- Application Areas:Home appliance components Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：--2 | 内部方法 | 0.10to0.50 | % |
| MD：3.20mm | 内部方法 | 0.10to0.50 | % | |
| TD：--2 | 内部方法 | 0.60to1.2 | % | |
| TD：3.20mm | 内部方法 | 0.50to1.1 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.23 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.060 | % | |
| MeltViscosity | 250°C,1500sec^-1 | ISO11443 | 210 | Pa·s |
| Melt Volume-Flow Rate (MVR) | 250°C/5.0kg | ISO1133 | 20.0 | cm3/10min |
| Melt mass flow rate | 250°C/5.0kg | ASTMD1238 | 27 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 6.50 | J |
| Bending strength 6, | ISO178 | 170 | Mpa | |
| Tensile modulus | ASTMD638 | 9900 | Mpa | |
| Bending modulus | ISO178 | 9400 | Mpa | |
| Suspended wall beam gap impact strength | 23°C | ISO180/1A | 7.0 | kJ/m² |
| -30°C | ISO180/1A | 7.0 | kJ/m² | |
| Unscented Izod Impact Strength | -30°C | ISO180/1U | 29 | kJ/m² |
| 23°C | ISO180/1U | 33 | kJ/m² | |
| Fracture bending strain | ISO178 | 2.0 | % | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/2U | 33 | kJ/m² |
| 23°C | ISO179/2U | 36 | kJ/m² | |
| FlexuralStrength | Yield,50.0mmSpan | ASTMD790 | 161 | Mpa |
| Tensile strength | Yield | ASTMD638 | 105 | Mpa |
| Tensile modulus | ISO527-2/1 | 10400 | Mpa | |
| tensile strength | Yield | ISO527-2/5 | 112 | Mpa |
| Break | ASTMD638 | 105 | Mpa | |
| Break | ISO527-2/5 | 112 | Mpa | |
| elongation | Yield | ASTMD638 | 2.0 | % |
| Yield | ISO527-2/5 | 2.0 | % | |
| Break | ASTMD638 | 2.0 | % | |
| Break | ISO527-2/5 | 2.0 | % | |
| Bending modulus | 50.0mmSpan | ASTMD790 | 9100 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | -- | ASTMD152513 | 202 | °C |
| -- | ISO306/A50 | 219 | °C | |
| -- | ISO306/B50 | 206 | °C | |
| -- | ISO306/B120 | 206 | °C | |
| -- | ASTMD152512 | 215 | °C | |
| RTIElec | UL746 | 130 | °C | |
| RTIStr | UL746 | 140 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 2.7E-05 | cm/cm/°C |
| MD：-40to150°C | ASTME831 | 2.2E-05 | cm/cm/°C | |
| MD：-40to40°C | ISO11359-2 | 3E-05 | cm/cm/°C | |
| MD：23to80°C | ISO11359-2 | 2.2E-05 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 9.1E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 7.6E-05 | cm/cm/°C | |
| TD：-40to150°C | ASTME831 | 7.7E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7.1E-05 | cm/cm/°C | |
| RTI Imp | UL746 | 140 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 216 | °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 219 | °C | |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 204 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 201 | °C | |
| Ball Pressure Test | 125°C | IEC60695-10-2 | Pass |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot wire ignition | HWI | UL746 | PLC0 | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC0 | |
| Arc resistance | ASTMD495 | PLC6 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC2 | |
| Dielectric strength | 3.20mm,in Oil | ASTMD149 | 21 | KV/mm |
| 3.20mm,inAir | ASTMD149 | 21 | KV/mm | |
| Leakage Trace Index | IEC60112 | 300 | V | |
| Volume resistivity | IEC60093 | 1.0E+15to1.0E+16 | ohms·cm | |
| ASTMD257 | 1.0E+15to1.0E+16 | ohms·cm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot filament ignition temperature | 0.8mm | IEC60695-2-13 | 775 | °C |
| 3.0mm15 | IEC60695-2-13 | 775 | °C | |
| UL flame retardant rating | 0.75mm | UL94 | V-0 | |
| 3.0mm | UL94 | 5VA | ||
| Burning wire flammability index | 0.75mm | IEC60695-2-12 | 960 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.