PBT Ultradur® B4040G3 BASF GERMANY
136
Unit Price:$4168 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 11MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Food contact compliance
- Application Areas:Home appliance components Business equipment
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | ISO294-4 | 0.40 | % |
| free,longitudinal | 0.21 | % | ||
| free,transverse | 1.1 | % | ||
| TD | ISO294-4 | 0.90 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.40 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.20 | % | |
| Apparent density | 0.70到0.80 | g/cm³ | ||
| Melt Volume-Flow Rate (MVR) | 275°C/2.16kg | ISO1133 | 22.0 | cm3/10min |
| Stickiness | ISO307 | 105 | cm³/g | |
| density | ISO1183 | 1.47 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 5.5 | kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 40 | kJ/m² |
| 23°C | ISO179/1eU | 40 | kJ/m² | |
| Ball pressure hardness | H358/30 | ISO2039-1 | 190 | Mpa |
| Tensile modulus | ISO527-2 | 7500 | Mpa | |
| tensile strength | Break | ISO527-2 | 120 | Mpa |
| elongation | Break | ISO527-2 | 2.8 | % |
| Bending modulus | ISO178 | 7010 | Mpa | |
| bending strength | ISO178 | 190 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature | ISO11357-3 | 223 | °C | |
| Maximum operating temperature - sortcycle operation | 210 | °C | ||
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 215 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 180 | °C | |
| specific heat | 1100 | J/kg/°C | ||
| Linear coefficient of thermal expansion | MD：23to80°C | ISO11359-2 | 2.0E-5到3.0E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative permittivity | 100Hz | IEC60250 | 3.70 | |
| 1MHz | IEC60250 | 3.50 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 300 | V |
| Surface resistivity | IEC60093 | 1E+13 | ohms | |
| Volume resistivity | IEC60093 | 1E+16 | ohms·cm | |
| Dissipation factor | 100Hz | IEC60250 | 1.4E-03 | |
| 1MHz | IEC60250 | 0.018 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flammability level | 0.75mm | IEC60695-11-10,-20 | HB | |
| 1.6mm | IEC60695-11-10,-20 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.