PBT VALOX™ Resin 420-7001 SABIC INNOVATIVE US
145
Unit Price:$3929 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25.2MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | MD：--4 | 内部方法 | 0.50to0.80 | % |
| MD：--2 | 内部方法 | 0.30to0.70 | % | |
| MD：3.20mm | 内部方法 | 0.30to0.80 | % | |
| MD：--3 | 内部方法 | 0.30to0.50 | % | |
| 吸水率 | 平衡,23°C,50%RH | ISO62 | 0.080 | % |
| 特定体积 | ASTMD792 | 0.660 | cm³/g | |
| 收缩率 | TD：--3 | 内部方法 | 0.40to0.60 | % |
| TD：--2 | 内部方法 | 0.50to1.0 | % | |
| TD：--5 | 内部方法 | 0.60to0.90 | % | |
| 熔体质量流动速率 | 250°C/2.16kg | ISO1133 | 17 | g/10min |
| 熔体体积流动速率 | 250°C/2.16kg | ISO1133 | 13.0 | cm3/10min |
| 收缩率 | TD：3.20mm | 内部方法 | 0.50to1.0 | % |
| 吸水率 | 24hr | ASTMD570 | 0.090 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 弯曲强度9, | ISO178 | 195 | Mpa | |
| 悬壁梁缺口冲击强度 | -30°C | ISO180/1A | 7.0 | kJ/m² |
| 洛氏硬度 | R级 | ISO2039-2 | 118 | |
| 球压硬度 | H358/30 | ISO2039-1 | 122 | Mpa |
| 无缺口伊佐德冲击强度 | 23°C | ISO180/1U | 45 | kJ/m² |
| 装有测量仪表的落镖冲击 | 23°C,TotalEnergy | ASTMD3763 | 8.00 | J |
| 拉伸强度 | 屈服 | ISO527-2/5 | 125 | Mpa |
| 伸长率 | 断裂 | ISO527-2/5 | 2.0 | % |
| 洛氏硬度 | R级 | ASTMD785 | 118 | |
| 拉伸强度 | Break | ASTMD638 | 120 | Mpa |
| 拉伸模量 | ASTMD638 | 9300 | Mpa | |
| 拉伸应变 | Break | ASTMD638 | 2.7 | % |
| 拉伸强度 | 断裂 | ISO527-2/5 | 125 | Mpa |
| 弯曲模量 | 50.0mmSpan | ASTMD790 | 7580 | Mpa |
| ISO178 | 8500 | Mpa | ||
| 伸长率 | 屈服 | ISO527-2/5 | 2.0 | % |
| 泰伯耐磨性 | 1000Cycles,1000g,CS-17转轮 | ASTMD1044 | 19.0 | mg |
| 简支梁缺口冲击强度 | -30°C | ISO179/1eA | 5.0 | kJ/m² |
| FlexuralStrength | Break,50.0mmSpan | ASTMD790 | 190 | Mpa |
| 拉伸模量 | ISO527-2/1 | 9300 | Mpa | |
| 拉伸应变 | Yield | ASTMD638 | 2.7 | % |
| FlexuralStrength | Yield,50.0mmSpan | ASTMD790 | 195 | Mpa |
| 简支梁无缺口冲击强度 | -30°C | ISO179/1eU | 45 | kJ/m² |
| 无缺口伊佐德冲击强度 | -30°C | ISO180/1U | 45 | kJ/m² |
| 拉伸强度 | Yield | ASTMD638 | 120 | Mpa |
| 简支梁无缺口冲击强度 | 23°C | ISO179/1eU | 45 | kJ/m² |
| 简支梁缺口冲击强度 | 23°C | ISO179/1eA | 5.0 | kJ/m² |
| 悬壁梁缺口冲击强度 | 23°C | ISO180/1A | 8.0 | kJ/m² |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | 0.45MPa,未退火,6.40mm | ASTMD648 | 216 | °C |
| Ball Pressure Test | 125°C | IEC60695-10-2 | Pass | |
| RTIStr | UL746 | 140 | °C | |
| 热变形温度 | 0.45MPa,未退火,3.20mm | ASTMD648 | 220 | °C |
| 线性热膨胀系数 | TD：-40到40°C | ASTME831 | 1.2E-04 | cm/cm/°C |
| MD：-40to40°C | ASTME831 | 2.5E-05 | cm/cm/°C | |
| 热变形温度 | 1.8MPa,未退火,6.40mm | ASTMD648 | 207 | °C |
| 线性热膨胀系数 | MD：60to138°C | ASTME831 | 2.5E-05 | cm/cm/°C |
| 热变形温度 | 1.8MPa,未退火,3.20mm | ASTMD648 | 203 | °C |
| 线性热膨胀系数 | TD：-40到40°C | ISO11359-2 | 1.2E-04 | cm/cm/°C |
| 维卡软化点 | ASTMD152514 | 215 | °C | |
| -- | ISO306/B120 | 215 | °C | |
| RTIElec | UL746 | 140 | °C | |
| RTI Imp | UL746 | 140 | °C | |
| 维卡软化点 | -- | ISO306/A50 | 223 | °C |
| -- | ISO306/B50 | 215 | °C | |
| 导热系数 | ISO8302 | 0.19 | W/m/K | |
| 热变形温度 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 217 | °C |
| 线性热膨胀系数 | MD：-40到40°C | ISO11359-2 | 2.5E-05 | cm/cm/°C |
| 热变形温度 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 204 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 介电强度 | 3.20mm,在油中 | IEC60243-1 | 16 | KV/mm |
| 耗散因数 | 1MHz | IEC60250 | 0.010 | |
| 耐电弧性 | ASTMD495 | PLC5 | ||
| 体积电阻率 | ASTMD257 | >3.2E+16 | ohms·cm | |
| 介电常数 | 1MHz | ASTMD150 | 3.70 | |
| 耗散因数 | 100Hz | ASTMD150 | 2E-03 | |
| 介电强度 | 1.60mm,在油中 | IEC60243-1 | 24 | KV/mm |
| 漏电起痕指数 | IEC60112 | 300 | V | |
| 耗散因数 | 100Hz | IEC60250 | 1E-03 | |
| 60Hz | IEC60250 | 1E-03 | ||
| 高电压电弧起痕速率 | HVTR | UL746 | PLC1 | |
| 体积电阻率 | IEC60093 | >1.0E+15 | ohms·cm | |
| 相比耐漏电起痕指数 | CTI | UL746 | PLC0 | |
| 介电常数 | 100Hz | ASTMD150 | 3.80 | |
| 相对电容率 | 60Hz | IEC60250 | 3.10 | |
| 耗散因数 | 50Hz | IEC60250 | 1E-03 | |
| 介电强度 | 3.20mm,inAir | ASTMD149 | 19 | KV/mm |
| 耗散因数 | 1MHz | ASTMD150 | 0.020 | |
| 表面电阻率 | IEC60093 | >1.0E+15 | ohms | |
| 介电强度 | 1.60mm,在油中 | ASTMD149 | 25 | KV/mm |
| 0.800mm,在油中 | IEC60243-1 | 28 | KV/mm | |
| 相对电容率 | 50Hz | IEC60250 | 3.10 | |
| 介电强度 | 1.00mm15 | IEC60243-1 | 19 | KV/mm |
| 相对电容率 | 1MHz | IEC60250 | 3.10 |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 灼热丝易燃指数 | 1.0mm | IEC60695-2-12 | 750 | °C |
| UL阻燃等级 | 0.8mm | UL94 | HB | |
| 极限氧指数 | ASTMD2863 | 19 | % |
| 补充信息 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 填充物 | ASTMD229 | 30 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.