Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Filler: Glass fiber reinf 30% filler by weight
- Application Areas:Automotive sector currency
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTMD792,ISO1183 | 1.53 | g/cm³ | |
| Melt mass flow rate | ASTMD1238 | 16 | g/10min | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.20 | % |
| flow | ASTMD955 | 0.30到0.50 | % | |
| Vertical flow direction | ISO294-4 | 0.70到1.1 | % | |
| Flow direction | ISO294-4 | 0.30到0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 23°C | ASTMD638 | 9650 | Mpa | |
| 80°C | ASTMD638 | 4830 | Mpa | |
| 121°C | ASTMD638 | 3760 | Mpa | |
| -- | ISO527-2/1A/1 | 9200 | Mpa | |
| Broken- 40°C | ASTMD638 | 190 | Mpa | |
| Fracture, 0 ° C | ASTMD638 | 159 | Mpa | |
| Fracture, 23 ° C | ASTMD638 | 134 | Mpa | |
| Fracture, 80 ° C | ASTMD638 | 77.2 | Mpa | |
| Fracture, 121 ° C | ASTMD638 | 61.4 | Mpa | |
| crack | ISO527-2/1A/5 | 130 | Mpa | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 45 | kJ/m² |
| 23°C | ISO179/1eU | 46 | kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 7.5 | kJ/m² |
| Rockwell hardness | M-Sale | ISO2039-2 | 90 | |
| -40°C | ASTMD638 | 11000 | Mpa | |
| 0°C | ASTMD638 | 10500 | Mpa | |
| Bending modulus | 23°C | ISO178 | 9700 | Mpa |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 8.5 | kJ/m² |
| Broken- 40°C | ASTMD638 | 1.9 | % | |
| Fracture, 0 ° C | ASTMD638 | 1.9 | % | |
| Fracture, 23 ° C | ASTMD638 | 2.0 | % | |
| Fracture, 80 ° C | ASTMD638 | 3.9 | % | |
| Fracture, 121 ° C | ASTMD638 | 4.3 | % | |
| crack | ISO527-2/1A/5 | 2.5 | % | |
| bending strength | 23°C | ISO178 | 210 | Mpa |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 8.5 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | TD | ISO11359-2 | 1E-04 | cm/cm/°C |
| Melting temperature | ISO11357-3,ASTMD3418 | 225 | °C | |
| vicat softening point | ISO306/B50 | 220 | °C | |
| Glass transition temperature | ISO11357-2 | 60.0 | °C | |
| 8.0Mpa, unannealed | ISO75-2/C | 150 | °C | |
| 1.8MPa, unannealed | ISO75-2/A | 205 | °C | |
| ASTMD648 | 206 | °C | ||
| 0.45MPa, annealed | ASTMD648 | 228 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 2.5E-05 | cm/cm/°C |
| 0.45MPa, unannealed | ISO75-2/B | 225 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 1MHz | ASTMD150 | 3.70 | ||
| 100Hz | IEC60250 | 4.50 | ||
| -- | IEC60243-1 | 31 | KV/mm | |
| ASTMD149 | 22 | KV/mm | ||
| IEC60093 | >1.0E+15 | ohms·cm | ||
| ASTMD257 | 1E+15 | ohms·cm | ||
| 1MHz | IEC60250 | 4.10 | ||
| ASTMD150,IEC60250 | 0.016 | |||
| 100Hz | IEC60250 | 2.2E-03 | ||
| Leakage Trace Index | IEC60112 | 425 | V | |
| Surface resistivity | IEC60093 | >1.0E+15 | ohms |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.710mm | UL94 | HB | |
| Extreme Oxygen Index | ISO4589-2 | 20 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.