PBT Cristin® SK603 BK851 DUPONT USA
152
Unit Price:$3168 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 44.9MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Filler: Glass fiber reinf Good strength (glass fibe 20% by weight ratio) 20% filler by weight
- Application Areas:Automotive Applications Electronic and electrical Industrial applications Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 吸水率 | -，23C/59RH | ISO 62 | 0.15 | % |
| -，Sat/23C | ISO 62 | % | ||
| 收缩率 | -，Across Flow | ISO 294-4 | 1.0 | % |
| -，Flow | ISO 294-4 | % | ||
| 密度 | ISO 1183 | 1.45 | g/cm | |
| MeltDensity | 1.26 | g/cm³ | ||
| 顶出温度 | 170 | °C | ||
| SpecificHeatCapacityofMelt | 1860 | J/kg/°C | ||
| 密度 | ISO1183 | 1.45 | g/cm³ | |
| 收缩率 | TD | ISO294-4 | 1.1 | % |
| MD | ISO294-4 | 0.30 | % | |
| 吸水率 | 饱和,23°C,2.00mm | ISO62 | 0.40 | % |
| 平衡,23°C,2.00mm,50%RH | ISO62 | 0.15 | % | |
| ThermalConductivityofMelt | 0.25 | W/m/K |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 拉伸模量 | ISO527-2 | 7000 | Mpa | |
| 拉伸强度 | 断裂 | ISO527-2 | 120 | Mpa |
| 伸长率 | 断裂 | ISO527-2 | 3.2 | % |
| TensileCreepModulus | 1hr | ISO899-1 | 7200 | Mpa |
| 拉伸蠕变模量 | 1000hr | ISO899-1 | 5600 | Mpa |
| 简支梁缺口冲击强度 | -，23℃, Type 1, Edgewise, Notch A | ISO 179 | 7.5 | KJ/m |
| 断裂点拉伸应力 | 23℃ | ISO 527-1, -2 | Mpa | |
| 断裂点拉伸应变 | 23℃ | ISO 527-1, -2 | 3.2 | % |
| 拉伸模量 | 23℃ | ISO 527-1, -2 | Mpa | |
| 弯曲模量 | 23℃ | ISO 178 | Mpa | |
| 弯曲强度 | 23℃ | ISO 178 | 180 | Mpa |
| 非缺口冲击强度 | 23 ℃, Type 1 | ISO 180 | 44 | KJ/m |
| 缺口冲击强度 | 23 ℃, Type 1, Notch A | ISO 180 | KJ/m | |
| 拉伸蠕变模量 | -，1h | ISO 899-1 | Mpa | |
| -，1000h | ISO 899-1 | Mpa | ||
| Charpy 非缺口冲击强度 | -，-30℃, Type 1, Edgewise | ISO 179 | 54 | KJ/m |
| -，23 ℃, Type 1, Edgewise | ISO 179 | 56 | KJ/m | |
| 简支梁缺口冲击强度 | -，-30 ℃, Type 1, Edgewise, Notch A | ISO 179 | KJ/m | |
| 弯曲模量 | ISO178 | 6500 | Mpa | |
| 弯曲强度 | ISO178 | 180 | Mpa | |
| 简支梁缺口冲击强度 | -30°C | ISO179/1eA | 9.0 | kJ/m² |
| 23°C | ISO179/1eA | 8.0 | kJ/m² | |
| 简支梁无缺口冲击强度 | -30°C | ISO179/1eU | 55 | kJ/m² |
| 23°C | ISO179/1eU | 60 | kJ/m² | |
| 悬壁梁缺口冲击强度 | -30°C | ISO180/1A | 8.0 | kJ/m² |
| 23°C | ISO180/1A | 9.0 | kJ/m² | |
| 悬臂梁无缺口冲击强度 | -30°C | ISO180/1U | 60 | kJ/m² |
| 23°C | ISO180/1U | 60 | kJ/m² |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 线性热膨胀系数 | 平行流动方向，23 to 55℃(73 to 130°F) | cm/cm/℃ | ||
| 垂直流动方向，23 to 55℃(73 to 130°F) | cm/cm/℃ | |||
| 热变形温度 | -，0.45 Mpa，未退火 | ℃ | ||
| -，1.80 Mpa，未退火 | ℃ | |||
| 阻燃等级 | -，0.750 mm | UL 94 | HB | |
| -，1.50 mm | UL 94 | HB | ||
| -，3.00 mm | UL 94 | HB | ||
| 熔融温度 | ISO 3146 | 225 | ℃ | |
| 热变形温度 | 0.45MPa,未退火 | ISO75-2/B | 220 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 204 | °C | |
| 维卡软化点 | ISO306/B50 | 210 | °C | |
| 熔融温度 | ISO11357-3 | 224 | °C | |
| 线性热膨胀系数 | MD | ISO11359-2 | 4E-05 | cm/cm/°C |
| TD | ISO11359-2 | 1E-04 | cm/cm/°C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 表面电阻率 | IEC60093 | 1E+15 | ohms | |
| 体积电阻率 | IEC60093 | >1.0E+15 | ohms·cm | |
| 介电强度 | IEC60243-1 | 29 | KV/mm | |
| 相对电容率 | 100Hz | IEC60250 | 4.00 | |
| 1MHz | IEC60250 | 3.60 | ||
| 耗散因数 | 100Hz | IEC60250 | 1.2E-03 | |
| 1MHz | IEC60250 | 0.019 | ||
| 漏电起痕指数 | IEC60112 | 350 | V |
| 其它性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 极限氧指数 | % |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 燃烧速率 | 1.00mm | ISO3795 | 28 | mm/min |
| UL阻燃等级 | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 极限氧指数 | ISO4589-2 | 19 | % | |
| FMVSS可燃性 | FMVSS302 | B | ||
| Fogging-G-value | condensate)4 | ISO6452 | 1E-04 | g |
| 补充信息 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 140 | µgC/g | |
| Odor | VDA270 | 3.00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.