PBT SHINITE® RG301 BK SHINKONG TAIWAN
224
Unit Price:$2169 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 250.2MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Carbon fiber reinforced
- Application Areas:Electronic and electrical Automotive Applications Automotive External Parts Parts under the hood of a Application in the automo
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTMD792 | 1.04 | g/cm³ | |
| ISO1183 | 1.04 | g/cm³ | ||
| Melt mass flow rate | 200°C/21.6kg | ASTMD1238 | 12 | g/10min |
| 220°C/10.0kg | ASTMD1238 | 8.0 | g/10min | |
| 220°C/10.0kg | ISO1133 | 8.0 | g/10min | |
| Shrinkage rate | MD | ASTMD955 | 0.50to0.80 | % |
| ISO294-4 | 0.50to0.80 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 屈服 | ASTMD638 | 46.6 | Mpa |
| 屈服 | ISO527-2 | 45.0 | Mpa | |
| elongation | 屈服 | ASTMD638 | 20 | % |
| 断裂 | ISO527-2 | 24 | % | |
| Bending modulus | ASTMD790 | 2110 | Mpa | |
| ISO178 | 2400 | Mpa | ||
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 19 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 240 | J/m |
| 23°C,6.40mm | ASTMD256 | 180 | J/m | |
| 23°C | ISO180/1A | 18 | kJ/m² | |
| bending strength | ISO178 | 70.0 | Mpa | |
| 屈服 | ASTMD790 | 63.7 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 106 | °C |
| vicat softening point | ISO306/B50 | 110 | °C | |
| Hot deformation temperature | 1.8MPa,未退火 | ASTMD648 | 100 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 94.0 | °C | |
| vicat softening point | ASTMD15252 | 110 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.