PBT Toraycon® 5201-X10-BK TORAY JAPAN
147
Unit Price:$3197 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 45MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant
- Application Areas:Automotive sector Electronic field Electrical field
- Color:--
- Grade:Impact resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | 80×80×3板材 | 2.0-2.5 | % | |
| Water absorption rate | 23℃·24hr | ASTM D-570 | 0.08 | % |
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 2.5 | % |
| MD:3.00mm4 | 内部方法 | 2.0 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.080 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2 | 2600 | Mpa |
| tensile strength | Yield,23°C | ISO527-2 | 50.0 | Mpa |
| elongation | Break,23°C | ISO527-2 | 50 | % |
| IZOD impact strength (1/8 hour width) | Notched，-40℃ | ASTM D-256 | 5.0 | kg.cm/cm |
| Bending modulus | 23℃ | ASTM D-790 | 23 | kg/cm |
| bending strength | 23℃ | ASTM D-790 | 770 | kg/cm |
| Fracture tensile elongation | 23℃ | ASTM D-638 | >150 | % |
| Under load | 4.6kg/cm | ASTM D-648 | 154 | °C |
| 18.6kg.cm | ASTM D-648 | 56 | °C | |
| Rockwell hardness | 23℃ | ASTM D-785 | 108 | |
| 23℃ | ASTM D-785 | 59 | M标度 | |
| tensile strength | 23℃ | ASTM D-638 | 490 | kg/cm |
| IZOD impact strength (1/8 hour width) | Unnotched，23℃ | ASTM D-256 | 不破裂 | kg.cm/cm |
| Unnotched，-40℃ | ASTM D-256 | 160 | kg.cm/cm | |
| Notched，23℃ | ASTM D-256 | 6.4 | kg.cm/cm | |
| Bending modulus | 23°C | ISO178 | 2400 | Mpa |
| bending strength | 23°C | ISO178 | 80.0 | Mpa |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 290 | kJ/m² |
| Rockwell hardness | M-Sale,23°C | ISO2039-2 | 70 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 150 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 55.0 | °C | |
| Linear coefficient of thermal expansion | MD：-30to100°C | ISO11359-2 | 1.4E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | 4E+16 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 19 | KV/mm | |
| Dielectric constant | 23°C,50Hz | IEC60250 | 3.40 | |
| 23°C,1kHz | IEC60250 | 3.50 | ||
| Dissipation factor | 23°C,50Hz | IEC60250 | 2E-03 | |
| 23°C,1MHz | IEC60250 | 0.020 | ||
| Arc resistance | IEC60950 | 130 | sec | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC0 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 8.70 | CM |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.