PBT Ultradur® B 4406 BASF GERMANY
150
Unit Price:$3860 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 46.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant
- Application Areas:Electrical components switch Laptop case
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.18mm | 0.15 | % | |
| Water absorption rate | Saturation | ASTMD570 | 0.40 | % |
| Saturation,23°C | ISO62 | 0.40 | % | |
| Equilibrium,50%RH | ASTMD570 | 0.25 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 0.25 | % | |
| Melt Volume-Flow Rate (MVR) | 250°C/2.16kg | ISO1133 | 30.0 | cm3/10min |
| Viscosity value | 降低的粘度 | ISO1628 | 122.0 | ml/g |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.4 | % | |
| density | ASTM D792/ISO 1183 | 1450 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 50 | kJ/m² |
| Tensile modulus | ASTM D638/ISO 527 | 3000 | kg/cm²(MPa)[Lb/in²] | |
| 23°C | ISO527-2 | 3000 | Mpa | |
| tensile strength | Yield,23°C | ASTMD638 | 65.0 | Mpa |
| Yield,23°C | ISO527-2 | 65.0 | Mpa | |
| elongation | Yield,23°C | ASTMD638 | 3.9 | % |
| Yield,23°C | ISO527-2 | 3.9 | % | |
| TensileCreepModule | 1hr | ISO899-1 | 1800 | Mpa |
| Nominal tensile fracture strain | -40°C | ISO527-2 | 3.3 | % |
| 23°C | ISO527-2 | 3.5 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1500 | mm/mm.℃ | |
| MD | ASTME831 | 9E-05 | cm/cm/°C | |
| MD | 5.5E-05 | cm/cm/°C | ||
| Melting temperature | ISO3146 | 223 | °C | |
| Peak melting temperature | ASTMD3418 | 223 | °C | |
| RTI Imp | 3.0mm | UL746 | 130 | °C |
| 0.75mm | UL746 | 130 | °C | |
| 1.5mm | UL746 | 130 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 60.0 | °C |
| 0.45MPa,Unannealed | ASTMD648 | 165 | °C | |
| 0.45MPa,Unannealed | ISO75-2/B | 170 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 80.0 | °C | |
| Combustibility (rate) | UL94 | V-0 | ||
| RTIElec | 0.75mm | UL746 | 125 | °C |
| 1.5mm | UL746 | 125 | °C | |
| 3.0mm | UL746 | 125 | °C | |
| RTIStr | 0.75mm | UL746 | 140 | °C |
| 1.5mm | UL746 | 140 | °C | |
| 3.0mm | UL746 | 140 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 100Hz | IEC60250 | 0.011 | |
| 1MHz | IEC60250 | 0.017 | ||
| Surface resistivity | IEC60093 | 1E+13 | ohms | |
| Dielectric constant | 100Hz | IEC60250 | 3.30 | |
| 1MHz | IEC60250 | 3.30 | ||
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| ASTM D257/IEC 60093 | 1E 14 | Ω.cm | ||
| Leakage Trace Index | IEC60112 | 250 | V | |
| VolumeResistivity | 1.50mm | ASTMD257 | >1.0E+15 | ohms·cm |
| SurfaceResistivity | 1.50mm | ASTMD257 | 1E+13 | ohms |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL94 | V-0 | |
| 0.75mm | UL94 | V-0 | ||
| 1.5mm | UL94 | V-0 | ||
| 3.0mm | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.