PBT DURANEX® 3300 JAPAN POLYPLASTIC
240
Unit Price:$3490 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced
- Application Areas:Automotive sector
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.53 | ||
| Water absorption rate | 23°C,24hr | ISO62 | 0.10 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | ISO527-2 | 140 | Mpa | |
| elongation | Break | ISO527-2 | 2.2 | % |
| Bending modulus | ISO178 | 9030 | Mpa | |
| elongation at break | ASTM D638/ISO 527 | 2.5 | % | |
| tensile strength | ASTM D638/ISO 527 | 132 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 9120 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 210 | kg/cm²(MPa)[Lb/in²] | |
| ISO178 | 220 | Mpa | ||
| Rockwell hardness | M-Scale | ISO2039-2 | 100 | |
| IZOD impact strength (with notch) | Notched侧 | ASTM D-256 | 93 | J/m |
| 反Notched侧 | ASTM D-256 | 530 | J/m | |
| elongation | ASTM D-638 | 2.5 | % | |
| tensile strength | ASTM D-638 | 132 | Mpa | |
| bending strength | ASTM D-790 | 210 | Mpa | |
| Bending modulus | ASTM D-790 | 9120 | Mpa | |
| Charpy impact strength | ASTM D256/ISO 179 | 93 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear expansion coefficient (room temperature) | 2-7 | |||
| Hot deformation temperature | 1.82MPa | ASTM D-648 | 213 | °C |
| Flame retardant grade | UL 94 | HB | ||
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 213 | °C |
| Linear coefficient of thermal expansion | MD：23to55°C | 内部方法 | 2E-05 | cm/cm/°C |
| TD：23to55°C | 内部方法 | 9E-05 | cm/cm/°C | |
| Hot deformation temperature | ASTM D648/ISO 75 | 213 | ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 2-7 | mm/mm.℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | 5E+16 | ohms·cm | |
| Dielectric strength | 3.00mm | IEC60243-1 | 23 | KV/mm |
| Leakage Trace Index | IEC60112 | 375 | V | |
| Volume resistivity | ASTM D257/IEC 60093 | 5×1016 | Ω.cm | |
| Volume resistivity | 3mmt | ASTM D-257 | 5×10 | Ω.cm |
| Dielectric breakdown strength | 2mmt | ASTM D-149 | 23 | MV/m |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ColourNumber | EF2001/ED3002 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Contact Us
Get App
Top