PBT Toraycon® 1494X02 TORAY JAPAN
139
Unit Price:$4350 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant
- Application Areas:Automotive sector Electronic field Electrical field
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.43 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.08 | % | |
| Under load | 4.6kg/cm | ASTM D-648 | 165 | °C |
| 18.6kg/cm | ASTM D-648 | 60 | °C | |
| Coefficient of friction | 金属 | ASTM D-1894 | 0.14 | |
| 本身 | ASTM D-1894 | 0.18 | ||
| Taber wear amount | 1.000g·CS-17轮 | ASTM D-1044 | 13 | 毫克/1.000m |
| Shrinkage rate | TD | ISO294-4 | 2.0 | % |
| Water absorption rate | (23°C,24hr) | ISO62 | 0.080 | % |
| 23℃·24hr | ASTM D-570 | 0.08 | % | |
| Shrinkage rate | 80×80×3板材 | 1.5-2.0 | % | |
| MD | ISO294-4 | 1.5 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 23℃ | ASTM D-638 | 620 | kg/cm |
| bending strength | 23℃ | ASTM D-790 | 940 | kg/cm |
| Bending modulus | 23℃ | ASTM D-790 | 28 | kg/cm |
| Rockwell hardness | ISO2039-2 | 82 | M（Scale） | |
| tensile strength | 23°C | ISO527-2 | 64.0 | Mpa |
| elongation at break | 23°C | ISO527-2 | 8.0 | % |
| Tensile modulus | 23°C | ISO527-2 | 3000 | Mpa |
| bending strength | 23°C | ISO178 | 105 | Mpa |
| Bending modulus | 23°C | ISO178 | 2900 | Mpa |
| Impact strength of simply supported beam gap | 23°C | ISO179/1eA | 2.5 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 66 | kJ/m² |
| compressive strength | 23℃ | ASTM D-695 | 930 | kg/cm |
| Fracture tensile elongation | 23℃ | ASTM D-638 | 20 | % |
| Rockwell hardness | ASTM D-785 | 119 | ||
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 30 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 20 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 90 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 35 | kg·cm/cm(J/M)ft·lb/in | ||
| elongation at break | ASTM D638/ISO 527 | 20 | % | |
| tensile strength | ASTM D638/ISO 527 | 65 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | M86 | ||
| Bending modulus | ASTM D790/ISO 178 | 2800 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 95 | kg/cm²(MPa)[Lb/in²] | |
| IZOD impact strength | Unnotched，23℃ | ASTM D-256 | 120 | kg·cm/cm |
| Unnotched，-40℃ | ASTM D-256 | 50 | kg·cm/cm | |
| Notched，23℃ | ASTM D-256 | 3.5 | kg·cm/cm | |
| Notched，-40℃ | ASTM D-256 | 3.0 | kg·cm/cm |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear thermal expansion | ASTM D-696 | 9.0 | cm/cm℃×10 | |
| Combustibility (rate) | UL94 | V-0 | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 9.0x10^-5 | mm/mm.℃ | |
| Hot deformation temperature | 0.45MPaUnannealed | ISO75-2/Bf | 136 | °C |
| 1.80MPaAnnealed | ISO75-2/Af | 64.0 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 9E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistance | IEC60093 | 2E+16 | Ω.cm | |
| Insulation strength | IEC60243-1 | 26 | KV/mm | |
| Dielectric constant | 23°C | IEC60250 | 3.40 | 1MHz |
| Dissipation factor | 23°C | IEC60250 | 0.020 | 1MHz |
| 耐电弧性 | IEC61621 | 70.0 | S | |
| Dielectric constant | ASTM D150/IEC 60250 | 3.4 | ||
| Volume resistivity | ASTM D257/IEC 60093 | 1.0x10^14 | Ω.cm | |
| Dielectric strength | 短时·23℃·1/8时 | ASTM D-149 | 17 | KV/mm |
| Volume resistivity | ASTM D-257 | 1.0 | cm×10 | |
| Arc resistance | ASTM D-495 | 70 | 秒 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fire rating | UL-94 | 1.50mm | V-0 | |
| UL-94 | 3.00mm | V-0 | ||
| UL-94 | 0.38mm | V-0 | ||
| UL-94 | 0.71mm | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.