PBT Toraycon® 5151G TORAY JAPAN
140
Unit Price:$3377 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 42.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant High impact resistance
- Application Areas:Electrical applications Electrical components
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.59 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.07 | % | |
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 1.9 | % |
| MD:3.00mm4 | 内部方法 | 1.4 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.070 | % |
| Shrinkage rate | 80×80×3板材 | 1.4-1.9 | % | |
| Water absorption rate | 23℃·24hr | ASTM D-570 | 0.07 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | 23℃ | ASTM D-785 | 85 | M标度 |
| Coefficient of friction | 金属 | ASTM D-1894 | 0.14 | |
| 本身 | ASTM D-1894 | 0.18 | ||
| IZOD impact strength (1/8 hour width) | Unnotched，23℃ | ASTM D-256 | 50 | kg.cm/cm |
| Unnotched，-40℃ | ASTM D-256 | 30 | kg.cm/cm | |
| Notched，23℃ | ASTM D-256 | 3.7 | kg.cm/cm | |
| Tensile modulus | 23°C | ISO527-2 | 5000 | Mpa |
| tensile strength | Yield,23°C | ISO527-2 | 55.0 | Mpa |
| elongation | Break,23°C | ISO527-2 | 4.0 | % |
| Bending modulus | 23°C | ISO178 | 4500 | Mpa |
| bending strength | 23°C | ISO178 | 97.0 | Mpa |
| Friction coefficient | 0.18 | |||
| Friction coefficient vs. Metal | SuzukiMethod | 0.14 | ||
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 45 | kJ/m² |
| Rockwell hardness | M-Sale,23°C | ISO2039-2 | 70 | |
| IZOD impact strength (1/8 hour width) | Notched，-40℃ | ASTM D-256 | 3.0 | kg.cm/cm |
| bending strength | 23℃ | ASTM D-790 | 930 | kg/cm |
| Bending modulus | 23℃ | ASTM D-695 | 750 | kg/cm |
| Fracture tensile elongation | 23℃ | ASTM D-638 | 6 | % |
| Bending modulus | 23℃ | ASTM D-790 | 46 | kg/cm |
| tensile strength | 23℃ | ASTM D-638 | 520 | kg/cm |
| Under load | 4.6kg/cm | ASTM D-648 | 192 | °C |
| 18.6kg.cm | ASTM D-648 | 85 | °C | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 35 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 30 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 50 | kg·cm/cm(J/M)ft·lb/in | ||
| elongation at break | ASTM D638/ISO 527 | 5 | % | |
| tensile strength | ASTM D638/ISO 527 | 55 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | M85 | ||
| Bending modulus | ASTM D790/ISO 178 | 4200 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 90 | kg/cm²(MPa)[Lb/in²] |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | ASTM D648/ISO 75 | 105 | ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 6.0x10^-5 | mm/mm.℃ | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 185 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 95.0 | °C | |
| Linear coefficient of thermal expansion | MD：-30to100°C | ISO11359-2 | 9.5E-05 | cm/cm/°C |
| Linear thermal expansion | ASTM D-606 | 6.0 | cm/cm×10 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric constant | ASTM D150/IEC 60250 | 3.5 | ||
| Volume resistivity | ASTM D257/IEC 60093 | 1.5x10^14 | Ω.cm | |
| IEC60093 | 3E+16 | ohms·cm | ||
| Dielectric strength | IEC60243-1 | 19 | KV/mm | |
| Dielectric constant | 23°C,50Hz | IEC60250 | 3.50 | |
| 23°C,1kHz | IEC60250 | 3.50 | ||
| Dissipation factor | 23°C,50Hz | IEC60250 | 2E-03 | |
| 23°C,1MHz | IEC60250 | 0.020 | ||
| Arc resistance | IEC60950 | 110 | sec | |
| Arc resistance | ASTM D-495 | 110 | 秒 | |
| Volume resistivity | ASTM D-257 | 1.5 | cm/cm×10 | |
| Dielectric strength | 短时·23℃·1/8时 | ASTM D-149 | 19 | KV/mm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 6.40 | CM |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.