PBT Toraycon® 5101G-30U TORAY JAPAN
161
Unit Price:$3305 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 70MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance Fast forming cycle
- Application Areas:Automotive Applications Electrical components
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 23℃,24hr | ASTM D570 | 0.07 | % |
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 1.0 | % |
| MD:3.00mm3 | 内部方法 | 0.40 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.070 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale,23°C | ISO2039-2 | 60 | |
| Tensile modulus | 23°C | ISO527-2 | 8500 | Mpa |
| tensile strength | 23°C | ISO527-2 | 130 | Mpa |
| elongation | Break,23°C | ISO527-2 | 4.0 | % |
| Bending modulus | 23°C | ISO178 | 8000 | Mpa |
| bending strength | 23°C | ISO178 | 205 | Mpa |
| Friction coefficient | 0.19 | |||
| Friction coefficient vs. Metal | SuzukiMethod | 0.15 | ||
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 65 | kJ/m² |
| tensile strength | 23℃ | ASTM D638 | 130 | Mpa |
| elongation | 23℃ | ASTM D638 | 5 | % |
| bending strength | 23℃ | ASTM D790 | 185 | Mpa |
| Bending modulus | 23℃ | ASTM D790 | 7.0 | GPa |
| Impact strength of cantilever beam gap | Notched，23℃ | ASTM D256 | 145 | J/m |
| Unnotched，23℃ | ASTM D256 | 85 | KJ/m | |
| Rockwell hardness | ASTM D785 | 89 | M | |
| friction coefficient | -，对金属 | ASTM D1894 | 0.15 | |
| -，对本身 | ASTM D1894 | 0.19 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | -，0.45MPa | ASTM D648 | 225 | °C |
| -，1.82Mpa | ASTM D648 | 215 | °C | |
| Linear coefficient of thermal expansion | ASTM D696 | 2.5 | ||
| Flame retardant grade | UL94 | HB | ||
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 205 | °C | |
| Linear coefficient of thermal expansion | MD：-30to100°C | ISO11359-2 | 4.2E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | 1E+17 | ohms·cm | |
| Dielectric constant | 23°C,50Hz | IEC60250 | 3.90 | |
| 23°C,1kHz | IEC60250 | 3.70 | ||
| Dissipation factor | 23°C,50Hz | IEC60250 | 2E-03 | |
| 23°C,1MHz | IEC60250 | 0.020 | ||
| Arc resistance | IEC60950 | 130 | sec | |
| Volume resistivity | ASTM D257 | 5.0 | ||
| Voltage endurance | ASTM D149 | 31 | MV/m | |
| Dielectric constant | -，50Hz | ASTM D150 | 3.9 | |
| -，10 | ASTM D150 | 3.7 | ||
| Tangent value of dielectric loss | -，50Hz | ASTM D150 | 0.002 | |
| -，10 | ASTM D150 | 0.02 | ||
| Arc resistance coefficient | ASTM D495 | 130 | S |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 6.70 | CM |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Contact Us
Get App