PBT Toraycon® 1101G-X54 TORAY JAPAN
150
Unit Price:$3274 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 90.1MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance Fast forming cycle Flame retardant Glass fiber reinforced
- Application Areas:Electrical field Electronic field Automotive sector
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.46 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.07 | % | |
| Water absorption rate | 23℃,24hr | ASTM D570 | 0.07 | % |
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 1.0 | % |
| Water absorption rate | 23°C,24hr | ISO62 | 0.070 | % |
| 23℃·24hr | ASTM D-570 | 0.07 | % | |
| Shrinkage rate | 80×80×3板材 | 0.4-1.0 | % | |
| Under load | 4.6kg/cm | ASTM D-648 | 220 | °C |
| 18.6kg.cm | ASTM D-648 | 210 | °C | |
| Shrinkage rate | MD:3.00mm4 | 内部方法 | 0.40 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| bending strength | 23°C | ISO178 | 190 | Mpa |
| IZOD impact strength (1/8 hour width) | Notched，-40℃ | ASTM D-256 | - | kg·cm/cm |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 65 | kJ/m² |
| bending strength | 23℃ | ASTM D-790 | 1700 | kg/cm |
| tensile strength | 23℃ | ASTM D-638 | 1200 | kg/cm |
| Fracture tensile elongation | 23℃ | ASTM D-638 | 5 | % |
| Rockwell hardness | 23℃ | ASTM D-785 | 89 | M标度 |
| Bending modulus | 23℃ | ASTM D-790 | 72 | kg/cm |
| IZOD impact strength (1/8 hour width) | Unnotched，23℃ | ASTM D-256 | 60 | kg·cm/cm |
| Unnotched，-40℃ | ASTM D-256 | - | kg·cm/cm | |
| Notched，23℃ | ASTM D-256 | 16 | kg·cm/cm | |
| elongation | Break,23°C | ISO527-2 | 3.5 | % |
| Friction coefficient vs. Metal | SuzukiMethod | 0.17 | ||
| Friction coefficient | 0.20 | |||
| Rockwell hardness | M-Sale,23°C | ISO2039-2 | 55 | |
| tensile strength | Yield,23°C | ISO527-2 | 120 | Mpa |
| Bending modulus | 23°C | ISO178 | 8000 | Mpa |
| Tensile modulus | 23°C | ISO527-2 | 8500 | Mpa |
| tensile strength | 23℃ | ASTM D638 | 120 | Mpa |
| elongation | 23℃ | ASTM D638 | 4 | % |
| bending strength | 23℃ | ASTM D790 | 175 | Mpa |
| Bending modulus | 23℃ | ASTM D790 | 7.6 | GPa |
| Impact strength of cantilever beam gap | Notched，23℃ | ASTM D256 | 185 | J/m |
| Notched，-40℃ | ASTM D256 | 135 | J/m | |
| Unnotched，23℃ | ASTM D256 | 60 | KJ/m | |
| Rockwell hardness | ASTM D785 | 90 | M | |
| friction coefficient | -，对金属 | ASTM D1894 | 0.17 | |
| -，对本身 | ASTM D1894 | 0.20 | ||
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 185 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 135 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 60 | kg·cm/cm(J/M)ft·lb/in | ||
| elongation at break | ASTM D638/ISO 527 | 4 | % | |
| tensile strength | ASTM D638/ISO 527 | 120 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | M90 | ||
| Bending modulus | ASTM D790/ISO 178 | 7600 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 175 | kg/cm²(MPa)[Lb/in²] |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 210 | ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 2.5x10^-5 | mm/mm.℃ | |
| Hot deformation temperature | -，0.45MPa | ASTM D648 | 220 | °C |
| -，1.82Mpa | ASTM D648 | 210 | °C | |
| Linear coefficient of thermal expansion | ASTM D696 | 2.5 | ||
| Flame retardant grade | UL94 | HB | ||
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 207 | °C |
| Linear coefficient of thermal expansion | MD：-30to100°C | ISO11359-2 | 4.2E-05 | cm/cm/°C |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
| Linear thermal expansion | ASTM D-696 | 2.5 | cm/cm℃×10 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTM D-257 | 7.5(2.2) | cm×10 | |
| Arc resistance | ASTM D-495 | 131 | 秒 | |
| Dielectric strength | 短时·23℃·1/8时 | ASTM D-149 | 27(18) | KV/mm |
| Dielectric constant | 23°C,1kHz | IEC60250 | 3.70 | |
| Dissipation factor | 23°C,50Hz | IEC60250 | 2E-03 | |
| Volume resistivity | IEC60093 | 1.4E+17 | ohms·cm | |
| Dielectric constant | 23°C,50Hz | IEC60250 | 3.80 | |
| Dielectric strength | IEC60243-1 | 28 | KV/mm | |
| Dissipation factor | 23°C,1MHz | IEC60250 | 0.020 | |
| Arc resistance | IEC60950 | 131 | sec | |
| Arc resistance coefficient | ASTM D495 | 131 | S | |
| Dielectric constant | ASTM D150/IEC 60250 | 3.8 | ||
| Volume resistivity | ASTM D257/IEC 60093 | 7.0x10^14 | Ω.cm | |
| ASTM D257 | 7.0 | |||
| Voltage endurance | ASTM D149 | 28 | MV/m | |
| Dielectric constant | -，50Hz | ASTM D150 | 3.8 | |
| -，10 | ASTM D150 | 3.7 | ||
| Tangent value of dielectric loss | -，50Hz | ASTM D150 | 0.002 | |
| -，10 | ASTM D150 | 0.02 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 7.50 | CM |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.