PPS Torelina® A400M D1 TORAY JAPAN
139
Unit Price:$4215 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Flame retardant Filler: Glass mineral 55% filler by weight
- Application Areas:Electrical applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | ASTM D-570 | 0.02 | % | |
| Flowing Long | 320℃,98MPa,1mm厚 | 东丽法 | 110 | |
| Shrinkage rate | Flow | 东丽法 | 0.15 | % |
| 垂重方向 | 东丽法 | 0.55 | % | |
| TD:3.00mm2 | 内部方法 | 0.75 | % | |
| MD:3.00mm4 | 内部方法 | 0.16 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.020 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | Yield,23°C | ISO527-2 | 170 | Mpa |
| elongation | Break,23°C | ISO527-2 | 1.3 | % |
| Bending modulus | 23°C | ISO178 | 18500 | Mpa |
| bending strength | 23°C | ISO178 | 255 | Mpa |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 30 | kJ/m² |
| Rockwell hardness | R-Scale | ISO2039-2 | 122 | |
| abrasion | ASTM D-1044 | 70 | mg/1000回 | |
| Curved elastic body | ASTM D-790 | 15.1 | GPa | |
| Fracture strength | ASTM D-732 | 65 | ||
| impact strength | Notched23℃ | ASTM D-256 | 100 | J/m |
| Unnotched23℃ | ASTM D-256 | 25 | KJ/m | |
| hardness | ASTM D-785 | 122 | 洛氏 | |
| bending strength | ASTM D-790 | 190 | Mpa | |
| tensile strength | ASTM D-638 | 145 | Mpa | |
| Limit PV value | 东丽法 | 815 | KJ/m | |
| tensile strength | ASTM D-638 | 1.3 | % | |
| friction coefficient | 对钢 | ASTM D-1894 | 0.28 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility | UL-94 | V-0 | ||
| Line expansion coefficient | Flow | ASTM D-696 | 1.7 | |
| 垂重方向 | ASTM D-696 | 2.5 | ||
| Rongdian | DSC | 278 | °C | |
| Hot deformation temperature | 1.82MPa | ASTM D-648 | >260 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 260 | °C | |
| Melting temperature | ISO11357-3 | 278 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.8E-05 | cm/cm/°C |
| TD | ISO11359-2 | 3E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | 1E+16 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 22 | KV/mm | |
| DielectricConstant | 23°C,1MHz | IEC60250 | 4.90 | |
| Dissipation factor | 23°C,1MHz | IEC60250 | 2E-03 | |
| Inherent resistance of volume | ASTM D-257 | 10 | Ω.m | |
| Arc resistance W level | ASTM D-495 | 128 | 秒 | |
| Induced positive connection | 10 | ASTM D-150 | 0.002 | |
| permittivity | 10 | ASTM D-150 | 5.0 | |
| Insulation breakdown voltage | ASTM D-149 | 15 | MV/m |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.36mm | UL94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| BarFlowLength | 320°C,1.00mm | 内部方法 | 115 | mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.